Using alkali treatment solution, neutrality treatment solution and acid treatment solution, the surface corrosion layer of copper plates and bronze plates that have been artificially corroded using HCl, H2SO4 and HNO3 solutions were removed. In the case of alkali treatment solution, only air oxidation in the form of black tenorite and white cuproous chloride remained without being removed. In the case of using a neutrality treatment solution, a anhydrous type layer of reddish brown cupric chloride remained without being removed, together with this black and white corrosion substance. In the case of using an acid treatment solution, this red corrosion substance also remained, but all of the oxide was removed on the surface of the specimen that was treated by alternatively using alkali treatment solution and acid treatment solution. In the case of this treatment solution with the order of alkali-acid, oxidation no longer proceeded only through the distilled water cleaning process after treatment, thereby showing that oxidation from the cleaning solution no longer proceeded.

Lead (II) ion selective poly(aniline) solid contact electrode based on Tetramethylthiuram monosulfide ionophore as a sulfur containing sensing material is successfully developed. The electrode exhibits good linear response of 25.6 mV / decade (at 20±0.2℃, r2=0.995) within the concentration range of 1.0×10-1~4.0×10-7 M Pb (II). The composition of this electrode was Ionophore : PVC : dioctylphthalate : potassiumtetrakis(4-chlorophenyl)borate : Oleic acid = 5.0 : 20.0 : 25.0 : 4.0 : 5.0. When we consider the results of using different composition electrodes based on only one potassiumtetrakis(4-chlorophenyl)borate or Oleic acid liphophlic additive, poly(aniline) solid contact electrode based on Tetramethylthiuram monosulfide ionophore with potassiumtetrakis(4-chlorophenyl)borate and Oleic acid liphophlic additive had the best result in response characteristics. The electrode shows good selectivity for lead (II) ion in comparison with alkali, alkaline earth, transition and heavy metal ions. This electrode is suitable for use with aqueous solutions of pH 3.0 ~ 7.0 and their standard deviation in the measured emf differences was ±2.94 mV at Tris buffered lead sample solution of 1.0×10-2 M and ±2.82 mV at Tris buffered lead sample solution of 1.0×10-3 M. Their stabilization time was less than 710 s. and response time was less than 16 s.