The damaged spent fuel rods must be stabilized by encapsulation or dry re-fabrication technologies before geological disposal. For applying the dry re-fabrication technology, we manufactured a vertical type furnace to perform the fuel material recovery from damaged fuel rods by oxidative decladding technology. As driving forces to accelerate oxidative decladding rate, magnetic vibration and pulse hammering generated by a pneumatic cylinder were used in this study. The oxidative decladding efficiency and recovery rate of fuel oxide powder with rod-cut length, oxidation temperature and time, oxygen concentration, and gas mixtures were investigated using simfuel rod-cuts in a vertical furnace for fuel material recovery and powder quality improvement. The oxidative decladding was performed for 2.5-10 h as following operation parameters: simfuel rod-cut length of 50-200 mm, oxidative temperature from 450 to 580°C, oxygen concentration of 49.5 or 75.6%, and gas mixtures in O2/Ar or O2/N2. In magnetic vibration, oxidative decladding was progressed only at bottom portion of fuel rodcut. Whereas, oxidative decladding in pulse hammering was occurred at both top and bottom portions of fuel-rod. In pulse hammering method, the oxidative decladding conditions to declad rod-cuts of 50- 200 mm in length were established to achieve both decladding efficiency of ~100% and fuel material recovery rate of > 99%. These conditions were as follows: oxidation temperature and time at 500°C and 2.5-10 h, oxygen concentration at 75.6% under O2/N2 gas mixtures. As operation conditions for a pneumatic cylinder, stroking, actuating, and waiting times were 0.5, 3, and 12 s.

Ag-containing aluminosilicate sorbents capable of capturing iodine were prepared by sol-gelation from Na, Al, and Si alkoxides using co-solvent exchange, Ag/Na ion exchange, solvent exchange, and ambient-pressure drying. The Na+AlSi-OH gel was prepared using sodium methoxide (NaOMe): aluminum tri-sec-butoxide (Al(OsBu)3): tetraethyl orthosilicate (TEOS) molar ratios of 1.05:1:1, 1.3:1.1:1, 1.5:1.3:1. The solvent effect on textural properties such as Brunauer-Emmett-Teller (BET) surface areas and pore size distributions and Ag0 particle sizes was investigated using water with high surface tension, isopropanol and n-heptane with low surface tension. The BET surface area, average pore size, and cumulative pore volume for sorbents strongly increased with decreasing surface tension of solvents and increasing Al/Si atomic ratios. In addition, Ag0 particle sizes increased with decreasing surface tension of solvents.

The damaged spent fuel rods must be stabilized by encapsulation or dry re-fabrication technologies before geological disposal. For applying the dry re-fabrication technology, we manufactured a vertical type furnace to perform both fuel material recovery from damaged fuel rods by oxidative decladding and sinterability improvement of fuel powder by repetition of oxidative and reaction treatment. A horizontal type furnace provides only a diffusion-controlled reaction resulting in longer reaction time and decreasing amount of powder for oxidation and reduction, whereas a vertical type furnace with a submerged gas distributor gives rapid reaction due to flowing gas-solid contact by fluidization. For observation of fluidization behaviors of uranium oxides at room temperature, fluidized column was prepared with transparent cylindrical tube, pressure transmitter and gas flow meter. Number of size of orifice holes was determined by equations in Fluidization Engineering [D.Kunii, O. Levenspiel]. Before uranium oxide test, as surrogates, WO2 (10.8 g/cm3) and Ta2O5 (8.2 g/cm3) powder similar to density of UO2 (10.96 g/cm3) and U3O8 (8.3 g/cm3), respectively were used to achieve fluidization operation conditions in the region from minimum to expanded fluidization. Fluidization behaviors and pressure drop of powder bed was observed according to operation parameters such as gas velocity, number and size of orifice holes, and powder amount.