GNPs have several excellent mechanical properties including high strength, a good young’s modulus, thermal conductivity, corrosion resistance, electronic shielding, etc. In this study, CF/GNP/Epoxy composites were manufactured using GNP weight ratios of 0.15 wt%, 0.3 wt%, 0.5 wt%, 0.7 wt% and 1 wt%. The composites were manufactured with a mechanical method (3-roll-mill). Tensile, impact and wear tests were performed according to ASTM standards D3039, D256 and D3181, respectively. The results show that the CF/GNP0.3wt%/Epoxy composites have good mechanical properties, e.g., tensile strength and impact and wear resistance. In this study, both carbon fabric and GNPs were used as reinforcements in the composites. The mechanical properties increased and weight loss decreased as the GNP content in the resin films was increased.

심층혼합처리공법에서 원지반과 개량재에 의해 형성되는 혼합처리토에 산업폐기물중 하나인 폐타이어와 기존 토목공사에서 섬유보강재로 사용되고 있는 강섬유를 혼합하여 보강재 및 개량재의 혼합비에 따른 개량체의 압축강도 특성을 파악하기위해 실내실험을 실시하였다. 개량재(시멘트, 시멘트계 고화재)의 경우는 건토중량에 대한 혼합비를 5%, 10%, 15%로 하였으며, 보강재(폐타이어, 강섬유)의 경우는 건토중량에 대한 혼합비를 0.5%, 1%, 2%로 하였다. 그 결과 개량재의 혼합비가 증가함에 따라 일축압축강도는 증가하였으며, 보강재를 첨가한 경우에는 폐타이어분말의 입자크기와 강섬유의 형상비가 작을수록 강도가 크게 나타났으며, 첨가량이 많아질수록 강도가 저하되는 경향이 나타났다.