Spinnable mesophase pitch precursor containing more than 98% mesophase content was successfully prepared from FCC-DO (fluid catalytic cracking-decant oil) without hydrogenation or catalytic reaction. The preparation method involved thermal condensation, vacuum treatment, and annealing treatment. Petroleum mesophase pitch-based carbon fibers are produced by melt spinning of pitch precursors, followed by stabilization and carbonization. The resulting carbon fiber exhibited good mechanical performances up to tensile strength of 2.1 GPa and tensile modulus of 212 GPa, with strain-to-failure higher than 1.0%. These properties ensuring that the automotive grade carbon fibers can be successfully prepared from FCC-DO derived petroleum mesophase pitches through the cost-competitive processes.

Petroleum-based impregnating pitches were prepared from pyrolysis fuel oil (PFO) using a two-step heat treatment without a separation process. The pressurized heat treatment, the first step, was used to improve the properties of the pitches and enhance the product yield by promoting the cracking and polymerization of the components in the PFO. An atmospheric heat treatment as the second step was used only to synthesize the impregnating pitches from the liquid pitches prepared during the first step. The prepared impregnating pitches had the properties of a commercial petroleum-based impregnating pitch. The impregnation performance was evaluated by HT-XRD and an impregnation test. The HT-XRD results showed changes in the stacked structure of the pitches at the impregnation temperature. The bulk density of the carbon block was increased to 14.3% and the porosity was reduced by 10.3% after the impregnation/recarbonization process. The high reaction temperature during the first step induced the formation of quinoline insoluble (QI) components during the second step of the treatment, and the QI components adversely affected the impregnation process.

Structural characterization of pyrolysis fuel oil (PFO) was conducted via 1H NMR and 13C NMR to elucidate its molecular structure and evaluate the feasibility of using PFO as a raw material for mesophase pitch synthesis. The average structural parameters were calculated based on the data from elemental analysis and matrix-assisted laser desorption/ionization time of flight mass spectrometry (MALDI-TOF-MS), as well as 1H NMR and 13C NMR data. The resultant structural features of PFO were compared with those of fluidized catalytic cracking-decant oil (FCC-DO). Based on the calculated parameters, we proposed average molecular models of PFO and FCC-DO. The molecular model of PFO showed that it had an aromatic structure consisting of three aromatic rings and one naphthenic ring fused with one pericondensed and two catacondensed aromatic carbons, as well as a short alkyl side chain (with only a methyl group). This structural feature of PFO demonstrated that it is highly favorable for use as a raw material for mesophase pitch synthesis. The empirical findings in this study provide an in-depth understanding of the molecular structure of PFO as well as FCC-DO and can offer insights for future research on the utilization of PFO and other petroleum heavy oils.

Pitch precursors affording excellent spinnability, high-level oxidation-resistance, and good carbonization yields were prepared by bromination–dehydrobromination of various ratios of pyrolyzed fuel oil and coal tar pitch. The pitches exhibited spinnabilities that were much better than those of pitches prepared via simple distillation. A pitch prepared using a 1:2 ratio of fuel oil and coal tar pitch exhibited the best tensile strength. Pitch fibers of diameter 8.9 ± 0.1 μm were stabilized at 270 °C without soaking time after heating at a rate of 0.5 °C/min and carbonized at 1100 °C for 1 h after heating at 5 °C/min. The resulting carbon fibers exhibited a tensile strength, elongation, Young’s modulus, and average diameter of 1700 ± 170 MPa, 1.6 ± 0.1%, 106 ± 37 GPa, and 7.1 ± 0.2 μm, respectively.