In order to investigate functional groups on the surface of Multi-walled Carbon Nanotubes (MWCNTs) induced by oxyfluorination, XPS (X-ray photoelectron spectroscopy) analysis was carried out. All core level spectra of MWCNTs were deconvoluted to several Pseudo-Voigt functions (sum of Gaussian-Lorentzian functions). Both O1s and F1s binding energy of oxyfluorinated MWCNTs shifted high value as increment of fluorine mixing ratio. The carbon-fluorine covalent bonding concentration increased as increment of fluorine mixing ratio. The shape and intensity of OF10-MWCNTs are similar with those of as-received MWCNTs. However, the intensity and binding energies of main peak position of OF20-MWCNTs and OF30-MWCNTs were dramatically increased by oxyfluorination.
The effect of cobalt precursor on the structure of Co supported multi-walled carbon nanotubes (MWCNTs) were studied by using X-ray photoelectron spectroscopy (XPS). MWCNTs were treated with a mixture of nitric and sulfuric acids and decorated with cobalt and/or cobalt oxides via aqueous impregnation solutions of cobalt nitrate or cobalt acetate followed by reduction in hydrogen. XPS was mainly used to investigate the phase of cobalt on MWCNTs after reduction with H2 flow at 400℃ for 2 h. Higher cobalt-nanoparticle dispersion was found in the MWCNTS prepared via cobalt nitrate decomposition. A typical XPS spectrum of Co 2p showed the peaks at binding energy (BE) values equal to 781 and 797 eV, respectively. It is found that cobalt nitrate supported MWCNTs is more dispersive and have catalytic activity than that of cobalt acetate supported MWCNTs at same preparation condition such as concentration of precursor solution and reduction environment.