Glass fiber (GF) insulation is a non-combustible material, light, easy to transport/store, and has excellent thermal insulation performance, so it has been widely used in the piping of nuclear power plants. However, if the GF insulation is exposed to a high-temperature environment for a long period of time, there is a possibility that it may be crushed even with a small impact due to deterioration phenomenon and take the form of small particles. In fact, GF dust was generated in some of the insulation waste generated during the maintenance process. In the previous study, the disposal safety assessment of GF waste was performed under the abnormal condition of the disposal facility to calculate the radiation exposure dose of the public residing/ residents nearby facilities, and then the disposal safety of GF waste was verified by confirming that the exposure dose was less than the limit. However, the revised guidelines for safety assessment require the addition of exposure dose assessment of workers. Therefore, in this study, accident scenarios at disposal facilities were derived and the exposure dose to the workers during the accident was evaluated. The evaluation was carried out in the following order: (1) selection of accident scenario, (2) calculation of exposure dose, (3) comparison of evaluation results with dose limits, and confirmation of satisfaction. The representative accident scenarios with the highest risk among the facility accident were selected as; (a) the fire in the treatment facility, (b) the fire in the storage facility, and (c) fire after a collision of transport vehicles. The internal and external exposure doses of the worker by radioactive plume were calculated at 10m away from the accident point. In evaluation, the dose conversion factors ICRP-72 and FGR12 were used. As a result of the calculation, the exposure dose to workers was derived as about 0.08 mSv, 0.20 mSv, and 0.10 mSv, due to fire accidents (vehicle collision, storage facilities, treatment facilities). These were 0.2%, 0.4%, and 0.2% of the limit, and the radiation risk to workers was evaluated to be very low. The results of this study will be used as basic data to prove the safety of the disposal of GF waste. The sensitivity analysis will be performed by changing the radiation source and emission rate in the future.

Radioactive materials emitted from nuclear accident or decommissioning cause soil contamination over wide areas. In the event of such a wide area of contaminated soil, decontamination is inevitable for residents to reside and reuse as industrial land. There are many ways to decontaminate these contaminated soils, but in urgent situations, the soil washing, which has a short process period and relatively high decontamination efficiency, is considered the most suitable. However, the soil washing process of removing fine soil and cesium by using washing liquid as water and adding a flocculating agent (J-AF) generates slurry/sludge-type secondary waste (Cs-contaminated soil + flocculating agent). Since this form of sludge contaminants cannot be disposed, solidification is needed using an appropriate solidification agent to treat wastes for disposal. Therefore, this study devised a treatment method of contaminated fine soils occurring after the soil washing process. This investigation prepared the simulated wastes of contaminated fine soils generated after the soil washing, and pelletized the samples using a roll compactor under the optimum operating conditions. The optimum conditions of the device were determined in the pre-test. Roll speed, feeding rate, and hydraulic pressure were 1.5 rpm, 25 rpm, and 28.44 MPa, respectively. The waste forms were manufactured by incorporating created pellets (H 6.5 × W 9.4 mm) using polymers as solidification agents. Used polymers were main ingredient (YD-128), hardener (G-1034), and diluent (LGE). The optimum mixing ratio was YD-128 : G-1034 = 65 : 35 phr, and LGE was added in an amount of 10wt% of the total mixture. To confirm the disposal suitability of the manufactured waste forms, characterization evaluation was carried out (compressive strength, thermal cycling, immersion, and leaching test). Characterization evaluation revealed a minimum compressive strength of 23.1 MPa, far exceeding 3.44 MPa of the disposal facility waste acceptance criteria. Compressive strength increased to the highest value of 31.90 MPa after immersion test. To examine leaching characteristics, the pH, Electrical Conductivity (EC) and leachability index (􀜮􀯜) of leachates were identified. As results, pH and EC consistently increased or remained constant with leaching time. The average of Co, Cs and Sr nuclides was 17.76, 17.38 and 14.04, respectively, exceeding the value of 6 in the waste acceptance criteria. Effective waste treatment/ disposal can be achieved without increasing volumes of sludge/slurry by enhancing the technique of this research by performing additional studies in the future.