ZnS- composite is normally used for sputtering target. In recent years, high sputtering power for higher deposition rate often causes crack formation of the target. Therefore the target material is required that the sintered target material should have high crack resistance, excellent strength and a homogeneous microstructure with high sintered density. In this study, raw ZnS and ZnS- powders prepared by a 3-D mixer or high energy ball-milling were successfully densified by spark plasma sintering, the effective densification method of hard-to-sinter materials in a short time. After sintering, the fracture toughness was measured by the indentation fracture (IF) method. Due to the effect of crack deflection by the residual stress occurred by the second phase of fine , the hardness and fracture toughness reached to 3.031 GPa and , respectively

Various approaches have been proposed to increase the green density. Warm compaction method has been used for the reduction of residual stress, the improvement of magnetic properties and the higher densities. In this work, the effect of warm compaction on green density of Fe powder was investigated. After ball-milling of Fe oxide powder for 30 hours, Fe oxide powder was reduced through the hydrogen reduction process. The pure Fe powder and polymer binder were mixed by 3-D tubular mixer. And then the mixed powder was warm-compacted with various compaction pressure and binder contents. The green density of specimen was added polyvinyl binder was higher than any other specimens.

Magnetic properties of nanostructured materials are affected in complicated manner by their microstructure such as pain size (or particle size), internal strain and crystal structure. Thus, studies on the synthesis of nanostructured materials with controlled microstructure are necessary fur a significant improvement in magnetic properties. In the present work, nanostructured Fe-Co alloy powders with a grain size of 50 nm were successfully fabricated from the powder mixtures of (99.9% purity) and by chemical solution mixing and hydrogen reduction.