The use of dolomite refractories has increased during the past several years in the manufacturing of clean steel during the stainless steelmaking process. However, at the same time, the use of dolomite refractories has led to what is known as the skull formation. In the present work, to understand the skull formation, the wetting characteristics of dolomite substrates by liquid Fe-19wt%Cr-10wt%Ni alloys in various oxygen partial pressures were initially investigated at 1753K using the sessile drop technique. For comparison, the wetting characteristics of alumina substrates were investigated with the same technique. It was found that the wetting index, (1+cosθ), of dolomite is approximately 40% higher compared to those of alumina. In addition, the oxygen partial pressure to generate the surface oxide, which may capture the liquid metal on the refractory surface, for dolomite is much lower than that for alumina. From this study, it was concluded that the use of dolomite is much more closely associated with the skull formation compared to the use of alumina due to the stronger wettability and the surface oxide formation at a lower oxygen partial pressure of dolomite.

본 연구는 시각장애인의 감성적 특성을 밝혀 향후 웹 접근성 지침에 반영하기 위해 진행된 기초연구로, 통일한 청각적 자극에 대한 시각장애인과 일반인의 감성 반응을 비교하고 그 차이점을 알아보고자 진행되었다. 이러한 목적을 위하여 본 연구에서는 음악(Representation Sound)과 음향효과(Abstraction Sound)를 이용한 15개의 청각 자극과 긍정 및 부정 감성어휘를 이용한 11개의 감성평가 척도를 선정하여 웹 설문 시스템을 제작하였으며, 이를 활용하여 31명의 시각장애인과 53명의 일반인을 대상으로 준비된 청각 자극에 대한 감성 반응을 측정하였다. 예외적인 경우가 있기는 하지만 설문의 결과는 대부분의 경우에서 두 집단 간의 감성반응패턴이 일치하는 것으로 나타나, 장애인의 감성욕구가 일반인과 크게 다르지 않음을 보여주고 있다. 이러한 결과는 디자인에서 사용자의 감성을 중요시 하는 것과 마찬가지로 웹 접근성에 대한 연구에서 장애인의 감성적 욕구가 중요시 되어야 함을 보여주고 있는 것이다.