Correlations between in-flight particle, splat and coating microstructure of thermally sprayed Ni20Cr were investigated. Flame spray and arc spray systems were employed for spraying Ni20Cr powder and Ni20Cr wire, respectively. The results showed that the arc spray process produced a broader size distribution for both in-flight particles and splats compared to flame process. Flower-like splat morphology was obtained from the arc spray whereas a pancake-like splat was obtained by flame spray. Ni20Cr coating sprayed by arc process had a denser microstructure, lower porosity and better adhesion at the interface.