Sugarcane bagasse has been used as a substrate for the development of microporous nano-activated carbons for the treatment and elimination of dissolved materials from aquatic environment. The activated carbon was produced using chemical activation in one-step method with zinc chloride ( ZnCl2) as the activating agent at a carbonization temperatures range from 500 to 900 °C. The effects of temperature and time of carbonization on the activated carbon product properties were thoroughly studied. The activated carbons that resulted were characterized using the N2 adsorption/desorption isotherms, Brunauer–Emmett–Teller method (BET), pore property analysis, micropore (MP) surface area, t-plot surface area, TGA, FTIR, SEM, TEM, and EDX analyses. The prepared activated carbon’s point of zero charge, Boehm titration process, iodine removal percentage, and methylene blue number were also investigated. The prepared activated carbon’s maximum surface area was achieved using a 2/1 impregnation ratio (dried sugarcane bagasse/ZnCl2) at 600 °C temperature of carbonization and 60 min residence time. 1402.2 m2/ g, 0.6214 and 1.41 cm3/ g, respectively, were the largest surface area, total pore volume, and micropore volume. As the activation temperature increased, the total pore volume increased and the BET study measured a pore diameter of 0.7 nm and a mean pore diameter of 1.77 nm.

The production of macroalgae-derived adsorbent is of great importance to realize the idea of treating pollutants with invaluable renewable materials. Herein, a novel meso-micro porous nano-activated carbon was prepared from green alga Ulava lactuca in a facile way via chemical activation with zinc chloride. The resultant activated carbon possesses a significant specific surface area 1486.3 m2/ g. The resulting activated carbon was characterized and investigated for the adsorption of Direct Red 23 (DR23) dye from an aqueous environment. Batch method was conducted to study the effects of different adsorption processes on the DR23 dye adsorption from water. Isotherms and kinetics models were investigated for the adsorption process of DR23 dye. It was found that the adsorption data were well fitted by Langmuir model showing a monolayer adsorption capacity 149.26 mg/g. Kinetic experiments revealed that the adsorptions of DR23 dye can be described with pseudo-secondorder model showing a good correlation (R2 > 0.997). The prepared activated carbon from Ulava lactuca was exposed to a total of six regeneration experiments. The regeneration result proved that the fabricated activated carbon only loses 19% of its adsorption capacity after six cycles. These results clearly demonstrated the high ability of the obtained active carbon to absorb anionic dyes from the aqueous environment.