SKD11 (ASTM D2) tool steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbide in the microstructure. SKD11 tool steel provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Adding of CNTs increased the performance of mechanical properties more. 1, 3 vol% CNTs was dispersed in SKD11 matrix by mechanical alloying. SKD11 carbon nanocomposite powder was sintered by spark plasma sintering process. FE-SEM, HR-TEM and Raman analysis were carried out for the SKD11 carbon nanocomposites.

The synthetic behaviors of carbon nanotubes (CNTs) by Fe/MgO catalysts were investigated in 0~90 wt.% range of MgO mixture ratios by catalytic chemical vapor deposition (CCVD) process. The CNTs were synthesized with 40 minutes of synthetic time, and 923 K of synthetic temperature using 0.1 L/min of ethylene gas and 1.0 L/min of hydrogen gas as synthetic and carrier gas, respectively. As the increase of synthetic temperatures and times, the diameters of CNTs become thicker. The carbon yield showed in a parabolic curve as MgO content increased and the maximum carbon yield was obtained at 30 wt.% of MgO. There were no obvious changes in the diameters of CNTs respect to the change of MgO content. Fe/MgO CNTs showed good crystalinity by High Resolution Transmission Electron microscope (HR-TEM) analysis. The behaviors of Fe/MgO CNTs have a tendency of depending on synthetic time and temperature rather than MgO content.

The effect of compositions of Al2O3 in the mixed Fe/Al2O3 catalysts on the synthetic behaviors of carbon nanotubes (CNTs) by catalytic chemical vapor deposition (CCVD) process was investigated in wide range of the mixture ratios of support materials. CNTs were synthesized with Fe/Al2O3 catalysis under the condition of 40 min in synthetic time, and 923 K of synthetic temperature using C2H4 and H2 as synthetic and carrier gas, respectively. The carbon yield with the content of Al2O3 showed in a parabolic curve and the maximum carbon yield was 40 wt.% of Al2O3. As the mixture ratio of Al2O3 increased, decreasing tendency was observed in the diameter of CNTs. Specific surface areas of CNTs were increased with the increase of the mixture ratio of Al2O3.