For rear metallization with Al paste, Al back contacts require good passivation, high reflectance, and a processing temperature window compatible with the front metal. In this paper, the effect of the firing ambient during the metallization process on the formation of Al rear metal was investigated. We chose three different gases as ambient gases during the firing process. Using SEM, we observed the formation of a back surface field in N2, O2, and Air ambients. To determine the effect of the ambient on Voc, the suns-Voc tool was used. In this study, we described the mechanism of burn-out of organic materials in Al paste during the firing process. The oxygen ambient plays an important role in the burn-out process. We calculated the efficiency with obtained the back surface recombination velocities using PC1D simulation. It was found that the presence of oxygen during the firing process influenced the uniform back surface field because the organic materials in the Al paste were efficiently burned out during heating. The optimized temperature with oxygen flow shows an absolute efficiency of 19.1% at PC1D simulation.

바이오가스로부터 폴리설폰 분리막을 이용한 메탄 농축 특성을 수치해석 방법으로 분석하였다. 향류 흐름 분리막공정의 지배 방정식을 유도하고 무차원화 한 후 Compaq Visual Fortran 6.6 소프트웨어을 이용하여 공정모사하였다. 공급 기체의 메탄 몰분율이 0.5인 경우 주어진 전형적 운전조건 상태에서 분리막 길이에 따른 잔류 측의 메탄 몰분율은 시점에서 종점으로 이동하면서 0.5에서 0.8로 증가하였으며 공급유량 대비 잔류유량 비율은 1.0에서 0.57으로 감소하였다. 공급 메탄 몰분율을 0.9로 변화시킨 경우 잔류 측의 최종 메탄 몰분율은 0.93으로, 공급대비 잔류유량은 0.91로 증가하였다. 공급 측 압력이 증가하여 투과 측 압력 대 공급 측 압력 비 값이 0.33에서 0.17로 변경될 경우 단 수율이 0.1과 같이 낮은 영역에서는 잔류 측 메탄 농도 변화가 거의 없는 반면, 단 수율이 0.3과 같이 높은 영역에서는 증가함을 확인할 수 있었다. 분리막 면적이1.14 m2에서 2.57 m2로 증가되면 단 수율의 변화에도 불구하고 잔류 측 메탄 농도가 비교적 높게 유지됨을 알 수 있었다.