Spherical Ag powder was prepared in the system of by wet chemical reduction method. The size of Ag powder was increased as the reaction temperature and the concentration of reducing agent was decreased in the constant concentration of dispersion agent. Optimum conditions of producing Ag powder having of D50 was 1M of , 0.5M of , 1.5g of Gelatine in the room temperature.

In this study, high purity fine powders were prepared by SHS (Self-propagating High-temperature Synthesis). We would examinate the study of sintering properties and characteristics as a function of temperature with various additives (binder, sintering agent). In separately binder addition, the green and sintered density of specimen were increased as binder content increases. The increased porosity resulted in fine grain size due to the inhibition of grain boundary moving. The and MgO playa role of increasing dielectric constants at room temperature. These values were decreased at curie temperature. In case of , the Curie temperature was decreased. In this study, a high dielectric ceramic capacitor material with temperature stability was synthesized by using various additives