The effect of Cu content on microstructure and mechanical properties of nano-sized Cu dispersed nanocomposites was investigated. The nanocomposites with Cu content of 2.5 to were prepared by reduction and hot-pressing of powder mixtures. The nanocomposites with Cu content of 2.5 and exhibited the maximum fracture strength of 820MPa and enhanced toughness compared with monolithic . The strengthening was mainly attributed to the refinement of matrix grains. The toughening mechanism was discussed by the observed microstructural feature based on crack bridging

The microstructure and mechanical property of hot-pressed composites with a different temperature for atmosphere changing from H to Ar have been studied. When atmosphere-changed from H to Ar gas at 145, the hot-pressed composite was characterized by inhomogeneous microstructure and low fracture strength. On the contrary, when atmosphere-changed at low temperature of 110 the composite showed more homogeneous microstructure, higher fracture strength and smaller deviation in strength. Based on the thermodynamic consideration and microstructural analysis, it was interpreted that the Cu wetting behavior relating to the formation of CuAlO is probably responsible for strong dependence of microstructure on atmosphere changing temperature. The reason for a strong sensitivity of fracture strength and especially of its deviation to atmosphere changing temperature was explained by the microstructural inhomogeneity and by the role of CuAlO phase on the interfacial bonding strength.