In this study, pitch crosslinked by oxygen function groups was made into activated carbon (AC) and pore structure was observed. The oxygen functional groups were introduced by the addition of waste PET for pitch synthesis. Activation agent ratios used to obtain the AC during the activation process were 1:1, 1:2 and 1:4 (pitch:KOH, w/w). The oxygen content in the prepared pitch was characterized by elemental analysis. Also, the molecular weight of pitch was investigated by MALDITOF. Specific surface area and micropore volume of the prepared AC were determined by the argon adsorption–desorption analysis and calculated using the Brunauer–Emmett–Teller and Horvath–Kawazoe equations, respectively. Micropore fraction of PET-free AC was smaller than that of PET-added AC. At high activation agent ratio, mesopores were created when the micropore structure collapsed. However, in the PET-added AC, due to the oxygen crosslinking effect, the micropore structure and micropore size were maintained even at a high activation agent ratio. Therefore, PET AC was found to have a higher micropore fraction than that of PET-free AC.

Coke aggregates and carbon artifacts were produced to investigate the interactions of coke and pitch during the kneading process. In addition, the kneading ratio of the coke and binder pitch for the coke aggregates was controlled to identify the formation of voids and pores during carbonization at 900°C. Experiments and thermogravimetric analysis revealed that carbon yields were improved over the theoretical yield calculated by the weight loss of the coke and binder pitch; the improvement was due to the binding interactions between the coke particles and binder pitch by the kneading process. The true, apparent, and bulk densities fluctuated according to the kneading ratio. This study confirmed that an excessive or insufficient kneading ratio decreases the density with degradation of the packing characteristics. The porosity analysis indicated that formation of voids and pores by the binder pitch increased the porosity after carbonization. Image analysis confirmed that the kneading ratio affected the formation of the coke domains and the voids and pores, which revealed the relations among the carbon yields, density, and porosity.

신제품 또는 신기술의 개발은 기업의 생존과 직결한 문제로써 급변하는 경영환 경과 심화하는 경쟁 속에서 성과 창출과 향상에 대한 관심이 증대하고 있다. 그러나 중소기 업은 국가 경제에서 차지하는 위상에 비해 규모와 보유자원 등의 한계를 가지므로 국가에서 는 다양한 정책적 지원을 제공한다. 조직수명주기에 관한 연구에 따르면 성장단계별로 기업 의 한계와 애로사항이 다르므로 차별적 지원이 이루어져야 할 필요가 있음을 알 수 있다. ‘2011년 중소기업기술통계’에 응답한 2,575개 기업 자료를 대상으로 기술개발공정의 기술 능력 수준과 편차가 R&D 매출성과에 어떤 영향을 끼치는지 검증하였다. 분석 결과, 기술능 력 수준은 R&D 매출성과에 정(+)의 영향을 끼쳤다. 또한, 기술능력의 편차와 R&D 매출성과 간에 관계를 정부지원이 조절하는 것을 알 수 있었다. 하지만, 정부지원이 기술수준이 R&D 매출성과에 미치는 영향을 성장단계별로 다르게 조절할 것이라는 가설에 대한 실증 분석 결 과 성장단계별로 조절효과가 유의적으로 각각 다르게 나타났다. 연구의 이론적인 시사점은 성장단계를 고려하지 않은 단순한 역학관계를 떠나 좀 더 실제 로 복잡한 중소기업 환경을 직시할 수 있는 현실적인 인과 모형을 제시하였고, 따라서 다양 성을 다각적인 방법으로 측정하여 연구변수로 활용해야하는 당위성을 마련하였다. 또한 실 무적 시사점은 성장단계별 정부지원에 대한 정책을 차별적으로 수립할 수 있고, 각자 다른 성장단계에 있는 중소기업으로 하여금 맞춤식의 정책을 순응하도록 하여 정부지원금의 효과 적으로 사용할 수 있는 가이드라인을 제시하였다는 것이다.