The aim of this study is to evaluate the environmental impacts of recovery of valuable metals from the desulfurizing spent catalyst. Molybdenum, vanadium and nickel widely used in the area of catalysis. But the demand of these metals is full filled by industries. Every year, more than 18,000 tons spent catalysts are discarded. In most countries, spent catalyst is classified as a harmful waste. Thus, metal recovery from spent catalyst has been processed. The recovery process of molybdenum, vanadium and nickel from spent catalyst was mainly carried out wet process. However, this process are not suitable for economics and environmental aspects. Because environmental costs for removal of sulfur in the spent catalyst is high and huge amount of industrial wastewater occurs. Thus, it is necessary to develop a process which is efficient and does not cause pollution than the wet process. Thus, we have studied life cycle assessment about the dry process for the recovery of valuable metals.

This study investigates the ultimate strength and curling influence in single shear bolted connection with aluminum alloys(6061-T6) using finite element analysis. The applicability of numerical modeling was validated through the comparison of existing test results. Main variables are end distance and edge distance. Strength reduction ratio by curling was estimated quantatively and it is known that the curling reduced the ultimate strength by maximum 26%.

Aluminum angles are widely used as tension members with bolted connection in buildings. In current design specification for net tensile capacity, reduction factor (U) is usually used to account for the effects of shear lag and bending induced from load eccentricity. In this paper, an investigation on reduction factor (U) of bolted angle connections was conducted and focused on net section efficiency according to the change of plate thickness and bolt arrangement. Exception to some specimens with short end distance and 1x1 bolt arrangement, all most specimens failed by net tensile fracture accompanied by curling at outstanding leg. The value of curling deformation has increased with increase of end distance (e) and the curling influenced the fracture mode of bolted angle connection. Also, net section efficiency has tended to increase according to the increase of bolt number and plate thickness.

Recently, study on the application of sustainable materials to building and civil structure fields has been increased. Especially, the usage of aluminum alloys can improve durability of structures due to it’s high corrosion resistance. In this study, to investigate the ultimate behaviors such as ultimate strength and fracture mode of single shear bolted connections with aluminum alloys (7075-T6), experiments were conducted. Main variables are bolt arrangement and end distance parallel to the direction of load. As a result, the specimens failed by shear out fracture and block shear fracture and also the specimens with long end distance were accompanied by curling (out of plane deformation). The curling led to reduction of ultimate strength or rigidity. Futhermore, pattern of strain distribution was investigated according to curling occurrence.

전자현미분석외에 금-은 고용체의 금 또는 은 성분을 결정할 수 있는 간편하고도 신뢰성 높은 측정법 개발은 응용 광물학자들에게 오랜 연구과제가 되어 왔다. 이를 달성하기 위한 방법으로 정량적으로 측정할 수 있는 단위포 상수, 반사도, 비중, 미경도 측정연구를 실시하였다. 이 실험을 위해 순수한 원소 금과 은을 5 at.% 간격으로 혼합하여 시료를 제작한 후 석영관을 사용하여 진공하에서 밀봉하였다. 고온에서 가열하여 용융시킨 후 서냉하여 얻어진 반응물을 각종 현미경, X 선 회절분석기, 전자현미분석기, 반사도측정기, 비중저울, 미경도측정기를 사용하여 분석하였다. 직경이 114.6 nm 인 Debye-Scherrer 카메라를 사용해 얻은 X 선분말회절자료로 계산한 단위포 상수의 크기는 은함량이 증가함에 따라 일정하게 증가한다. 반사도 측정에는 480nm와 546nm 두파장을 사용하였는데 두 파장 모두에 대해 은 함량이 증가할수록 반사도가 증가한다. 또한 480nm를 사용했을 때의 반사도 변화가 현저하므로 유용하다. 비중은 은 함량이 증가할수록 오히려 일정하게 감소한다. 한편, 25g과 50g 추를 사용하여 측정한 미경도 값은 금-은고용체내의 성분변화에 관계없이 불규칙하게 변하여 어떤 경향을 나타내지 않는다.