A solution combustion process for the synthesis of hollandite (BaAl2Ti6O16) powders is described. SYNROC (synthetic rock) consists of four main titanate phases: perovskite, zirconolite, hollandite and rutile. Hollandite is one of the crystalline host matrices used for the disposal of high-level radioactive wastes because it immobilizes Sr and Lns elements by forming solid solutions. The solution combustion synthesis, which is a self-sustaining oxi-reduction reaction between a nitrate and organic fuel, generates an exothermic reaction and that heat converts the precursors into their corresponding oxide products in air. The process has high energy efficiency, fast heating rates, short reaction times, and high compositional homogeneity. To confirm the combustion synthesis reaction, FT-IR analysis was conducted using glycine with a carboxyl group and an amine as fuel to observe its bonding with metal element in the nitrate. TG-DTA, X-ray diffraction analysis, SEM and EDS were performed to confirm the formed phases and morphology. Powders with an uncontrolled shape were obtained through a general oxide-route process, confirming hollandite powders with micro-sized soft agglomerates consisting of nano-sized primary particles can be prepared using these methods.

저방사성폐수지, 제올라이트, 가연성잡고체 혼합폐기물을 유리화하기 위해서 AG8W1 후보 유리와 가연성잡고체 단독으로 유리화하기 위하여 DG-2 후보유리가 개발되었다. 두 후보유리의 화학적 내구성을 평가하기 위하여 PCT와 VHT 침출시험이 수행되었다. 7일 PCT 침출시험 수행결과 AG8W1과 DG-2의 주요 원소별 침출률은 기준유리(benchmark glass SRL-EA) 보다 낮게 나타남을 알 수 있었고 미국 Hanford 유리고화체 규제치 보다 낮은 결과를 나타냄을 알 수 있었다. 또한, 120일 동안의 시험에서도 주요 원소인 B, Na, Si, Li가 SRL-EA 보다 낮게 나타남을 볼 수 있었다. VHT 침출시험 수행결과 AG8W1, DG-2의 침출률(leach rate)은 각각 , 로써 미국 Hanford 규제치 보다 낮은 결과를 나타냈다. 결과적으로 유리화 시설 상용운전 시 사용예정인 이들 후보유리들의 침출은 안정화되어 있었으며 화학적 내구성이 우수함을 알 수 있었다.