The objective of this study is to investigated the compressive characteristics properties used cement paste containing Silica Fume Binder with elapsed curing time.

As an effort to enlarge the territory of the county, many researchers have been studying floating foundation system. The procedure to build such structure needs prestressing and the joint that unify the precast concrete modules. Most importantly, the performance of aqua-epoxy used joint between modules is a critical factor of the structure, thereby it is important to evaluate the performance of it. Hence, this study tests the performance of the joint due to the joint length and the material properties of aqua-epoxy. The result showed that the specimen of 1cm joint length using 2% silica-fume mixed aqua-epoxy has the optimum load carrying capacity.

In this study, KS F 2405 was used to investigated the compressive strength of property of high performance concrete (HPC) using the fly ash and silica fume. The experiments were carried out silica fume-binder ratio from 5% (SF5) and fly ash 25%+silica fume 5% (FA25SF5). The compressive strength of HPC determined on 7days and 28days.

본 연구에서는 실리카흄 대체재로 활용 가능한 실리카 흄 무혼입 결합재(SFFB)의 치환율에 따른 고강도 콘크리트의 품질특성을 비교․분석하기 위하여, 실리카흄, SFFB의 2수준과 물-결합재비는 25, 35% 치환율은 실리카 흄 10%, SFFB 5, 10 15(%)의 4수준으로 설정하였다. 실험을 실시한 결과, 목표 유동성을 확보하기 위한 고성능감수제의 첨가율은 물-결합재비가 낮을수록 증가하였으며, SFFB가 실리카 흄 보다 저흡수성을 갖는 재료적 특성으로 인해 고성능감수제의 첨가율이 감소하는 경향을 나타내었다. 압축강도에서는 SFFB 치환율이 10%일 경우 인장강도에서는 치환율이 15%일 경우 가장 우수한 강도를 나타내었으며, 자기수축에서는 W/B와 SFFB의 치환율과 상관없이 Plain(SF)에 비해 수축이 저감하는 것으로 나타났다.