When aluminum is in an alkaline state, the aluminum oxide film surrounding aluminum is dissolved and moisture penetrates the exposed aluminum surface, causing corrosion of aluminum. At this time, hydrogen gas is generated and there is a risk of explosion due to the generated hydrogen gas. Aluminum radioactive waste is difficult to permanently dispose of because it does not meet the standards for the acquisition of low- and intermediate-level radioactive waste cave disposal facilities currently managed and operated by the Korea Nuclear Environment Corporation. However, because of this risk, it is necessary to study how to safely treat and dispose aluminum waste. In this study, overseas cases were investigated and analyzed to ensure the safety of aluminum waste disposal, and the current status of aluminum radioactive waste generated during decommissioning of the Korea Research Reactor 1&2 and a treatment plan to secure disposal suitability were presented. The process of removing a little remaining oxygen in molten steel during the reduction of iron oxide in the iron refining process is called deoxidation, and a representative material used for deoxidation is aluminum. In the case of metal melting decontamination, which is one of the decontamination processes of radioactive metal waste, a method of treating aluminum waste by using aluminum as a deoxidizer is proposed.

TRIGA 연구로의 해체 시 발생하는 금속성 폐기물의 용융기술을 확립하기 위한 기초연구로 전기로 내에서 방사성 핵종(Co, Cs, Sr)을 포함한 알루미늄의 용융 시 용융온도, 용융시간 및 플럭스(flux)의 종류가 핵종의 분배 거동에 미치는 영향을 조사하였다. 플럭스의 종류에 따라 다소 차이는 있으나, 플럭스의 첨가로 알루미늄 용융체의 유동성이 증가됨을 확인할 수 있었다 용융 후주괴(ingot) 및 슬래그(slag) 시료의 XRD분석을 통해 핵종이 주괴에서 슬래그 상으로 이동하고 슬래그를 구성하고 있는 산화알루미늄과 결합하여 안정한 화합물을 형성함을 알 수 있었다. 슬래그의 발생량은 용융온도와 용융시간이 증가할수록 증가하는 경향을 보였으며, 증가속도는 플럭스의 종류에 따라 차이를 보였다. 핵종 중 Co는 용융온도가 증가함에 따라 주괴 내 에서는 감소하였으나 슬래그 상에서는 증가하는 경향을 보였으며, 실험조건에 따라 최대 90까지 주괴에서 슬래그로 이동하였다. 휘발성이 강한 Cs과 Sr은 대부분이 슬래그와 분진으로 이동하여 매우 높은 제염계수를 얻을 수 있었다.