In this study, the impact properties of aluminum honeycomb core composite are investigated through simulation analysis. The specimens are applied with different impact energies of 50 J, 70 J, and 100 J. The maximum load occurs at 3.7 ms for 50 J, 3.7 ms for 70 J and 2.3 ms for 100 J. The maximum load occurs when the striker is penetrating the upper face sheet in all cases. In case of 50 J impact energy, striker does not penetrate the lower face sheet and honeycomb core sandwich can be stable as the energy of 38 J happens. In case of 70 J impact energy, the striker penetrates into the specimen. The striker then causes the damage to the lower face sheet after penetrating the upper face sheet and the core as the energy of 53 J happens. In case of 100 J impact energy, the striker penetrates through all of the upper face sheet, core and lower face sheet as the energy of 65 J happens. This study can be utilized at the design of aluminum honeycomb core sandwich composite structure by understanding stability through the impact property.

본 논문에서 알루미늄 하니콤 샌드위치판 구조(AHSP)의 특성에 대해 해석한 결과는 다음과 같다. 1) AHSP의 H/T비가 낮아질수록 응력이 감소하며, 셀 크기(H)보다는 코어의 두께(T)가 두꺼워질수록 강도와 강성이 증가함을 알 수 있다. 2) AHSP 구조가 동일한 질량에서부터 증가하면서 EASP 구조에 비해 2.5～6.0배 정도의 높은 강도를 보이는 것을 알 수 있다. 3) AHSP의 면재의 두께변화는 AHSP 전체의 강성에 별로 영향을 미치지 못했으나, 심재의 두께가 증가할수록 단면 2차 모멘트의 값이 커지기 때문에 AHSP의 강성이 매우 커짐을 알 수 있다. 4) EASP보다 강성이 큰 AHSP의 고유진동수가 크며, 진동 모드 사이의 차도 커짐을 알 수 있다. 5) 비교연구 결과 AHSP 구조가 EASP 구조보다 적은 질량으로 훨씬 더 높은 강성을 갖는, AHSP 구조의 우수성이 입증된다. 따라서 중량경감이 가장 중요한 문제 중의 하나인 초고속선 및 대형선의 경우 AHSP 구조가 높은 굽힘강성을 갖고 다른 재료에 비해 상대적으로 적은 중량이 필요하므로 구조 재료로서의 적합성을 알 수 있다.