Anti-reflection coating films have used to increase the transmittance of displays and enhance the efficiency of solar cells. Hydrophobic anti-reflection coating films were fabricated on a glass substrate by sol-gel method. To fabricate an anti-reflection film with a high transmittance, poly ethylene glycol (PEG) was added to tetraethyl orthosilicate (TEOS) solution. The content of PEG was changed from 1 to 4 wt% in order to control the morphology, thickness, and refractive index of the SiO2 thin films. The reflectance and transmittance of both sides of the coated thin film fabricated with PEG 4 wt% solution were 0.3% and 99.4% at 500 nm wavelength. The refractive index and thickness of the thin film were n = 1.29 and d = 105 nm. Fluoro alkyl silane (FAS) was used for hydrophobic treatment on the surface of the anti-reflection thin film. The contact angle was increased from 13.2˚ to 113.7˚ after hydrophobic treatment.

VO2 써모크로믹 원도우의 가시광 투과율을 높히기 위하여 내마모성이 우수한 SiO2박막을 이용하여 AR(anti-rdflection)코팅을 하였다. 두가지 중요한 공정변수인 기판온도와 증착속도가 AR효과에 미치는 영향을 조사하였다. 그리고 SiO2박막의 AR효과는 낮은 기판온도와 높은 증착속도에서 더 우수한 것으로 나타났으며, 이는 SiO2AR 박막의 굴절율과 상관관계가 있는 것으로 나타났다. VO2 써모크로믹 유리 위에 SiO2AR-코팅을 했을 때 약 30% 정도의 가시광 투과율의 향상이 있었다. 그리고 AR-코팅을 하지 않은 경우보다 더 뚜렷한 써모크로미즘을 나타냈다. 또한 천이온도는 70˚C정도로 AR-코팅을 하지 않은 VO2써모크로믹 유리의 경우와 같게 나타났다.