The present work was performed to investigate the effect of coiling temperature on the annealed texture in Cu/Nb-added ultra-low-carbon steels. The ultra-low-carbon steels were coiled at 650 and 720˚C, respectively. The result showed that the Cu-added ultra-low-carbon steel at a low coiling temperature produced a desirable annealed texture related to good formability. On the other hand, Nb-added ultra-low-carbon steel at a high coiling temperature also produced a desirable texture. This is attributed to the effect of Nb, which retards recrystallization during the coiling process.

The texture and microstructure in Cu/Nb added ultra low carbon steels through the different thickness layer were studied after hot rolling. It was found that the two ultra low carbon steels all show the inhomogeneity of hot rolling texture and the Cu-added ultra low carbon steel was far more inhomogeneous than Nb-added one. In the center layer, the strong α fibre, γ fibre textures and the shear textures including 001<110>, 111<112> were founded. Near the surface, the α fibre texture and the orientation texture caused by a typical plane-strain deformation condition of bcc metals were observed.

극저탄소 알루미늄 킬드강내에 합금원소로 첨가된 Al, Ti, Nb, B등은 열처리 공정중 질화물이나 탄화물로 석출되어 강의 재결정집합조직을 변화시킴으로써 강판재의 디입드로잉 특성에 결정적인 영향을 미친다. 본 연구에서는 Ti및 Nb를 단독으로 또는 동시에 첨가한 데 이어, B, P, Si 및 Mn등을 추가로 첨가한 극저탄소 고강도 강판의 집삽조직에 미치는 질화물, 탄화물과 같은 미세 석출물의 영향을 TEM, SEM, 광학현미경분석에 의하여 조사하였다. Nb 및 Ti를 동시에 첨가한 강에서는 미세한 Nb2C 및 Ti2AIN가 주로 석출되는 반면, Nb를 단독으로 첨가한 강에서는 미세한 AIN 및 조대한 BN이 석출되고,Ti를 단독으로 첨가한 강에서는 비교적 조대한 Ti4N3및 조대한 N10N22/Ti68이 석출되는 것으로 관찰되었다. 또한 이러한 탄질화물들의 석출에 의하여 세 강이 서로 다른 결정입도를 나타내는데, 결정입도는 Nb 및 Ti동시첨가강과 Nb단독첨가강이 서로 비슷하고, Ti단독첨가강이 가장 큰 것으로 나타났다.