It has been well known that concrete structures exposed to chloride and sulfate attack environments lead to significant deterioration in their durability due to chloride ion and sulfate ion attack. The purpose of this experimental research is to evaluate the resistance against chloride ion and sulfate attack of the cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were cured in the water of 20±3℃ and immersed in fresh water, 10% sodium sulfate solution for 28 and 91 days, respectively. To evaluate the resistance to chloride ion and sulfate attack for the cementless concrete specimens, the diffusion coefficient for chloride ion and compressive strength ratio, mass change ratio, and length change ratio were measured according to the NT BUILD 492 and JSTM C 7401, respectively. It was observed from the test results that the resistance against chloride ion and sulfate attack of the cemetntless concrete were comparatively largely increased than those of OPC concrete with decreasing water-binder ratio.

초고성능 콘크리트와 고연성 무시멘트 복합재료는 높은 압축강도 및 높은 연성 등 재료의 우수한 성능으로 인하여 유망한 건설재 료로 분류되고 있다. 이 연구의 목적은 초고성능 콘크리트와 고연성 무시멘트 복합재료의 압축강도와 인장거동에 대하여 실험적으로 조사하 여 성능을 비교하는 것이다. 이를 위하여 밀도, 압축강도, 일축인장실험 등 일련의 실험을 수행하였다. 실험결과 알칼리 활성 슬래그 기반 고연 성 무시멘트 복합재료의 압축강도와 인장강도는 초고성능 콘크리트의 압축강도와 인장강도에 비하여 낮게 나타났지만, 인장하중 하에서 알칼 리 활성 슬래그 기반 고연성 무시멘트 복합재료의 인장변형성능 및 인성은 초고성능 콘크리트의 인장변형성능 및 인성에 비하여 높은 것으로 나타났다. 또한 알칼리 활성 슬래그 기반 무시멘트 페이스트에 폴리에틸렌섬유를 보강하여 7.89 %에 달하는 높은 인장변형성능을 확보할 수 있는 것으로 나타났다.