It has been well known that concrete structures exposed to chloride and sulfate attack environments lead to significant deterioration in their durability due to chloride ion and sulfate ion attack. The purpose of this experimental research is to evaluate the resistance against chloride ion and sulfate attack of the cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were cured in the water of 20±3℃ and immersed in fresh water, 10% sodium sulfate solution for 28 and 91 days, respectively. To evaluate the resistance to chloride ion and sulfate attack for the cementless concrete specimens, the diffusion coefficient for chloride ion and compressive strength ratio, mass change ratio, and length change ratio were measured according to the NT BUILD 492 and JSTM C 7401, respectively. It was observed from the test results that the resistance against chloride ion and sulfate attack of the cemetntless concrete were comparatively largely increased than those of OPC concrete with decreasing water-binder ratio.

최근 전세계적으로 3차원 객체 모델(3D Object Model)을 활용하여 건설 프로젝트의 생애주기 동안 참여주체들이 효과적으로 정보를 공유하고 관리할 수 있도록 하는 가상건설시스템의 개발이 활발히 진행되고 있다. 이 논문에서는 가상 공간에서 토목구조물의 해석 및 설계를 위하여 반드시 필요한 구조물의 3차원 객체모델과 구조해석 시스템과의 인터페이스 설계를 다루었다. 3D 객체모델 생성에 필요한 인관 매개변수모델링 기법과 구조물의 구조해석에 필요한 다양한 변수를 고려할 수 있는 제품계층구조(product breakdown structure, PBS) 구축 방안을 제시하였다. PBS 구성시 3D 객체 모델 정보로부터 구조 해석에 필요한 속성 정보만을 추출하여 해석 프로그램에 적용이 가능하게 하였으며, 협업작업에 의해 결정되는 여러 수치를 다시 객체정보로 추가 작업 없이 전달하여 3D 객체 모델과 연동되어 변화될 수 있는 인터페이스 프로그램 설계 방안을 제안하였다. 향후 이 연구의 결과를 기반으로 개발된 3D 객체모델과 구조해석 시스템의 인터페이스 프로그램이 가상건설 시스템 구현에 효과적으로 사용될 수 있을 것으로 판단된다.

본 연구에서는 실험을 통하여 자기치유 재료 혼입 모르타르 보의 자기치유 성능을 평가하였다. 실험에는 일반 모르타르 보 실험체와 자기치유 모르타르 보 실험체가 사용되었으며, 모르타르의 압축강도, 내력 및 균열의 자기치유 효과를 비교하여 자기치유 성능을 평가하였다. 실험결과 자기치유 재료를 혼입한 모르타르의 압축강도가 일반 모르타르의 압축강도보다 작았지만 28일 압축강도에 대한 118일 압축강도 비율은 동일하게 나타났다. 실험체의 내력은 재령일이 길어질수록 증가하는 경향을 나타냈다. 일반 모르타르 실험체는 균열이 발생할 경우 재령일이 증가하여도 하중은 회복되지 않았으나 자기치유 모르타르 실험체의 경우 반응 생성물의 영향으로 내력이 다소 회복되는 경향을 나타냈다. 균열폭은 두 종류의 실험체 모두 치유기간이 지난 후 감소하는 경향을 보였으나 자기치유 모르타르 실험체에서만 반응 생성물이 관찰되었다.

The purpose of this experimental research is to evaluate the long-term resistance against sulfate attack of the alkali activated cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were immersed in fresh water and 10% sodium sulfate solution for 28, 91, 182, and 365 days, respectively. To evaluate the long-term resistance to sulfate attack for the cementless concrete specimens, compressive strength ratio, mass change ratio, and length change ratio were measured according to the JSTM C 7401. It was observed from the test results that the resistance against sulfate attack of the cemetntless concrete was comparatively largely increased than that of OPC concrete irrespective of water-binder ratio.

In this study, high strength concrete with satuated artificial lightweight aggregate(SLWA) produced by domestic for reducing autogenous shrinkage, which provides additional water to the hydratin cement particles, is applied to be the internal curing. This paper presents the test result of basic property of SLWA and autogenous shrinkage with volumes of SLWA.

In this paper, the methodology to develop web-based assembly system with BIM(Building Information Modeling) technology for modular bridge is proposed. The system has three main parts that are composed of standardized part library, assemble module, and virtual construction. The web-based assembly design program for modular bridge could be widely used for rapid construction of bridges with module library information.