Cu matrix composites reinforced with chopped carbon fiber (CF), which is cost effective and can be well dispersed, are fabricated using electroless plating and hot pressing, and the effects of content and alignment of CF on the thermal properties of CF/Cu composites are studied. Thermal conductivity of CF/Cu composite increases with CF content in the in-plane direction, but it decreases above 10% CF; this is due to reduction of thermal diffusivity related with phonon scattering by agglomeration of CF. The coefficient of thermal expansion decreases in the in-plane direction and increases in the through-plane direction as the CF content increases. This is because the coefficient of thermal expansion of the long axis of CF is smaller than that of the Cu matrix, and the coefficient of thermal expansion of its short axis is larger than that of the Cu matrix. The thermal conductivity is greatly influenced by the agglomeration of CF in the CF/Cu composite, whereas the coefficient of thermal expansion is more influenced by the alignment of CF than the aggregation of CF.

Scale generation in the inside of a pipe IS restricted by reduction and oxidation(REDOX) reaction of alloyed metal of Cu-Zn. To measure the scale generating rate in the 1.67 mm of inside diameter of stainless steel tube, 300 ppm of CaCO3 solution is circulated in the REDOX reactor and stainless steel tube in the order. In the case of CaCO3 solution treated by REDOX reactor, flowing is maintained without plugging in the stainless steel tube, and the concentration of Cu and Zn in the circulating solution showed less than 1 ppm, which is equal to that of untreated by REDOX reactor. The crystal type of CaCO3 generated by crystalline nucleus of Cu or Zn, mostly showed aragonite type.

This study is focused on the antimicrobial activity of cyanobacteria Microcystis aeruginosa by the reduction and oxidation reaction of copper and zinc alloy metal fiber filter. Cu/Zn ion is easily makes radicals with molecular hydroperoxide. Especially, hydroperoxide radical shows strong toxicity to the strains. Plasma membrane causes conformational change when hydroperoxide radical binds to plasma membrane. Elution of copper ion from copper and zinc alloy metal fiber is detected in the cyanobacteria solution as 0.5 ppm, and that of zinc ion is 0 ppm respectively. Zinc ion is figured to form a hydroxide in the cyanobacteria solution and precipitated to form a sludge. The concentration of chlorophyll-a in the cyanobacteria solution was proved to be the index of antimicrobial level of Microcystis aeruginosa.