This article presents the successful consolidation of the mixed Co and Diamond powders for a drilling segment by the combined application of magnetic pulsed compaction (MPC) and subsequent sintering, and their properties were analyzed. Homogeneous hardness (Hv 220) and density (97%) of sintered bulks fabricated by MPC were obtained by the new technique, where higher pressure has been employed for short period of time than that of general process. A fine microstructure and homogeneous hardness in the consolidated bulk were observed without cracks. Relatively higher drilling speed of 9.61 cm/min and life time of 6.55 m were found to the MPCed specimens, whereas the value of the specimens fabricated by general process was 11.71 cm/min and 7.96 m, respectively. A substantial improvement of mechanical properties of segment was achieved through this study.

Diamond segments were fabricated by cold pressing and sintering under pressure at the temperature up to . Based on the results of this investigation, it can be concluded that the segments containing 39wt.% cobalt in the matrix material have the highest bending strength at a fracture probability of 50 % due to the weibull distribution method. According to the weibull statistics, it was also determined that the transverse rupture strength was the best for 39 wt.% cobalt ratio in the matrix material for the fracture probability when the other variables are the same.