Carbon micro particles with dimple patterns were produced by electro-spraying a solution of pitch in tetrahydrofuran. Particle formation depended on separation in an electrical field and volatilization of the solvent. More than 80% of the obtained carbon exhibited an average particle size of less than 50 μm. X-ray diffraction analysis suggests that the carbon with dimple patterns has increased crystallinity after heat treatment.

Fe-Cr-Al powder porous metal was manufactured by using new electro-spray process. First, ultra-finefecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid(0.05~0.5% powders) was dispersed on Polyurethane foam through the electro-spray process. And then degreasing andsintering processes were conduced. In order to examine the effect of cell size (200 µm, 450 µm, 500 µm) in process,pre-samples were sintered for two hours at temperature of 1450˚C, in H₂ atmospheres. A 24-hour thermo gravimetricanalysis test was conducted at 1000˚C in a 79% N₂ + 21% O₂ to investigate the high temperature oxidation behavior ofpowder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased withincreasing cell size. In the 200 µm porous metal with a thinner strut and larger specific surface area, the depletion ofthe stabilizing elements such as Al and Cr occurred more quickly during the high-temperature oxidation compared withthe 450, 500 µm porous metals.