In this study, we have prepared a Ti-6Al-4V/V/17-4 PH composite structure via a direct energy deposition process, and analyzed the interfaces using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The joint interfaces comprise two zones, one being a mixed zone in which V and 17-4PH are partially mixed and another being a fusion zone in the 17-4PH region which consists of Fe+FeV. It is observed that the power of the laser used in the deposition process affects the thickness of the mixed zone. When a 210 W laser is used, the thickness of the mixed zone is wider than that obtained using a 150 W laser, and the interface resembles a serrated shape. Moreover, irrespective of the laser power used, the expected  phase is found to be absent in the V/17-4 PH stainless steel joint; however, many VN precipitates are observed.

신 구 콘크리트의 부착강도 시험시 두 재료의 계면에서 파괴가 유도되어 순수한 부착강도를 측정할 수 있도록 계면에 원형의 비부착면을 삽입하여 직접인발시험에 의해 부착강도를 측정하는 실험방법을 제시하였다. 먼저, 새로 제안한 실험방법에 의해 계면에서 응력이 집중되는 정도를 파악하기 위해 유한요소해석을 수행하여 두 재료의 탄성계수비 및 비부착면의 면적 (균열률)에 따른 계면에서의 파괴에너지를 산정하였으며, 부재의 크기 및 하중에 대한 보정을 감안하여 무차원함수로 환산하였다. 그리고 본 연구에서 제시된 부착강도 시험방법의 신뢰성을 입증하기 위해, 3가지 크기의 원형 비부착면(균열률 0.2, 0.4. 0.6)이 삽입된 신 구 콘크리트 복합시편(유황 폴리머 콘크리트+보통 콘크리트)을 사용하여 부착강도를 측정하였고 앞서 전개된 무차원함수로부터 계면 파괴에너지를 역산하였다. 시험결과, 모든 시편이 계면에서 파괴가 유도되었다. 또한 실험 데이터 및 해석결과를 분석하여 균열률이 0.4~0.6인 경우에 부착강도의 오차가 가장 적게 발생될 수 있음을 파악하였다.

동전모양의 균열이 이상복합 실린더 계면에 존재하는 혼합모드 조건(I, II)에 대해 유한요소법을 사용하여 에너지해방율을 구하였다. 두재료의 탄성비와 노치율을 변화시켜 상업용 FEM 프로그램인 ABAQUS로부터 얻은 결과를 가상 균열법과 J 적분법에 적용하였으며 에너지해방율을 구하여 무차원함수로 표현하였다. 모드 II의 무차원 에너지해방율은 균열길이와 탄성비가 증가되면서 그 값이 증가됨을 알수 있었다. 반면, 모드 I의 무차원 에너지해방율은 탄성비가 증가하면서 그 값이 감소하며, 두재료의 탄성비가 3 이상인 경우에 균열길이가 증가되면서 무차원 에너지해방율이 감소하다가 다시 증가하게 나타났다. 또한 수치해석된 결과치를 무한판 실린더의 응력확대계수에 대한 정해와 비교하여 본 해석의 신뢰성을 확보하였다