우수한 열안정성과 낮은 구동전압을 가지면서 수명이 길고 발광 효율이 우수한 유기 EL 고분자인 PPV계열의 새로운 MEH-PPV[1,4-비스(브로모메틸)-2-(2-에틸헥실옥시)-5-메톡시벤젠] 주사슬에 2,5-비스(4-(브로모메틸)페닐)-1,3,4-옥사디아졸과 2,7-디브로모-9,9-디옥틸-9H-플루오렌을 첨가시켜 공중합하여MEH-O-DPPV 공중합체를 합성하였으며, 합성된 MEH-O-DPPV 공중합체가 기존의 MEH-PPV 동종중합체과 열적 안정성, 분광학적 특성 및 발광 특성을 비교 분석하였다. 합성된 MEH-O-DPPV 공중합체와 PMMA을 1:50중량비로 용액 제조 후 나노섬유를 만들어 광학 현미경으로 관찰하였다.

In this study, MEH-PPV was synthesized and MEH-PPV and its mixtures with PMMA were deposited on substrates with Langmuir-Blodgett(LB) technique and their photoluminescent char acteristics were investigated using UV-Vis absorption spectroscopy, and photoluminescence(PL) measurements. The surface morphology of the LB films of MEH-PPV and its mixture with PMMA were investigated using Atomic Force Microscopy(AFM). Electroluminescent devices using LB films were fabricated with Al and ITO as a top and bottom electrode, respectively, and their I-V characteristics were investigated.