Molten salts based on magnesium chloride can be used in the nuclear power reactor because they have a high heat capacity and heat stability, and allow for a faster neutron spectrum. However, magnesium chloride is highly hygroscopic, leading to the formation of moisture-related impurities, which result in the corrosion of structural materials and negatively affect the operation of the reactor. The dehydration of magnesium chloride is studied using both thermal and electrochemical treatments. According to previous studies, water impurities in magnesium chloride molten salt transform into magnesium oxide over 650 degrees Celsius. The temperature profile of the molten salt is suggested to separate magnesium chloride and magnesium oxide, focusing on cooling rate near the freezing point of magnesium chloride. Two layers separated by a phase boundary on the salt surface appear due to the density difference between magnesium oxide and magnesium chloride. Further, the removal of oxide ions remaining in the molten salt is carried out by electrochemical treatment. Two different cells, each consisting of two electrodes, are used. One cell is composed of graphite anode and nickel cathode. The other is composed of tin oxide anode and nickel cathode. As the reaction proceeds, carbon dioxide and oxygen are generated in graphite and tin oxide, respectively, and magnesium electrodeposition occurs at the cathode. The amount of purified magnesium oxide is measured to the endpoint, which is notified by the reduced current. The efficiency of each method is compared by measuring the weight ratio of the purified part to the unpurified part. Thermogravimetric analyzer (TGA) and UV-vis spectroscopy are used to check the quality of the purified part. Only magnesium oxide remains at a temperature above the boiling point of magnesium chloride. Therefore, the amount of magnesium oxide in the purified part can be measured by the mass change of the salt through the TGA method. For UV-vis spectroscopy, the transmittance is measured which depends on the weight percent of the impurities in the purified part. The suggested purification method using both thermal and electrochemical treatment is assessed quantitatively and qualitatively. It is expected that hygroscopic molten salts other than magnesium chloride will be able to be dehydrated through the above process.

In this study, chloride penetration in a repaired concrete using magnesium polymer ceramic (MPC) was assessed based on the NT BUILD 492. To investigate the effect of repaired material on chloride penetration, a cylinder OPC concrete specimen was fabricated and attached on the surface with MPC. Then, chloride penetration test was carried out on the combined concrete sample at a constant applied voltage (30 V) for 6 hours. It was found that most of chloride sources was passed though the interface between OPC and MPC, resulting in a loss of chloride in the material. Thus, it is needed to modify the conventional chloride penetration test for the repaired concrete specimen.