This study investigated the magnetic properties and frequency dispersion of complex permeability of Ni-Zn-Co ferrites used for magnetic shielding in near field communication (NFC) system. The sintered specimens of (Ni0.7Zn0.3)1-xCoxFe2O4 composition were prepared by the conventional ceramic processing. The coercive force and saturation magnetization were measured by vibrating sample magnetometer. The complex permeability was measured by RF impedance analyzer in the range of 1 MHz~1.8 GHz. The coercive force increased and saturation magnetization decreased with increasing the Co substitution. The real and imaginary parts of complex permeability decreased and the resonance frequency increased with Co substitution, which was attributed to the increase in crystal anisotropy field and reduction in saturation magnetization. The effect of Co substitution could be found in reducing the magnetic loss to nearly zero at the operating frequency of NFC (13.56 MHz).

산소 결핍 페라이트 (oxygen deficient ferrites, ODF) MeFe2O4-δ는 약 300˚C의 낮은 온도에서 CO2를 C와 O2로 분해한다. 본 연구에서는 (Nix, Zn1-xFe24 초미세 페라이트 분말을 수열합성법으로 제조하여 CO2 분해특성을 살펴보았다. 제조된 페라이트는 XRD 분석 결과, 페라이트의 전형적인 스피넬 구조를 보여주고 있으며, ICP-AES, EDS 정량분석에 의하여 초기 혼합 조성비와 거의 동일한 조성비로 합성되었음을 알 수 있었다. 제조된 (Ni, Zn)-ferrites 분말의 BET 비표면적은 약 110mg2/g 이상의 큰 값으로 나타났으며, 입자크기는 약 5~10nm로 매우 작았다. 산소결핍 페라이트 (Nix, Zn1-x)Fe2O4-δ</TEX>의 CO2 분해 효율은 조성에 따라 큰 차이를 보이지 않았으며 3원계 (Ni, Zn)-ferrite가 Ni-ferrite보다 더 높았다.