(Y123) powders for the fabrication of bulk superconductors were synthesized by the powder reaction method using (99.9% purity), (99.75%) and CuO (99.9%) powders. The raw powders were weighed to the cation ratio of Y:Ba:Cu=1:2:3, mixed and calcined at in air with intermediate repeated crushing steps. It was found that the formation of Y123 powder was more sensitive to reaction temperature than reaction time. The calcined Y123 powder and a mixture of (Y123 + 0.25 mole + 1 wt.% , (Y1.5)) were used as raw powders for the fabrication of poly-grain or single grain superconductors. The superconducting transition temperature () of the sintered Y123 sample was 91 K and the transition width was as large as 11 K, whereas the of the melt-grown Y1.5 sample was 90.5 K and the transition width was 3.5 K. The critical current density () at 77 K and 0 T of the sintered Y123 was 700 , whereas the of the top-seeded melt growth (TSMG) processed Y1.5 sample was . The magnetic flux density (H) at 77 K of the TSMG-processed Y123 and Y1.5 sample showed the 0.53 kG and 2.45 kG, respectively, which are 15% and 71% of the applied magnetic field of 3.5 kG. The high H value of the TSMG-processed Y1.5 sample is attributed to the formation of the larger superconducting grain with fine Y211 dispersion.

산화물 초전도체에 있어서 고천이 임계온도를 갖는 미소영역을 추출하여 이를 분석하기 위하여 La-Ba-Cu-O 계, Y-Ba-Cu-O 계 및 Bi-Pb-Sr-Ca-Cu-O 계의 초전도체를 고상법 및 nitrate solution method로 제조하였다. 제조된 시료들에 대해서 x선회절분석과 저항을 측정하였다. 이들 시료 중에서 고천이온도를 나타내는 미소부분을 Meissner효과를 이용한 추출법으로 분리 해내고 EDAX로 이를 분석하였으며, 이들 결과를 요약하면 다음과 같다. nitrate solution method를 적용하면 YBCO계에 있어서 비교적 단시간에 치밀한 미세조직을 갖는 천이 온도 90K의 초전도체를 제조할 수 있다. Meissner효과를 이용하여 고천이온도에서 추출해낸 미소영역의 EDAX분석 결과는 고상법을 사용한 YBCO-23S와 nitrate solution method으로 제조한 YBCO-23N 및 YBCO-36N 에서는 초기의 조성과 거의 같았으며, 고천이 온도에서 추출된 미소영역은 조성보다는 산소 결함의 차이에 기인한 것으로 생각된다. 공침법으로 제조한 YBCO-23NA 에서는 과도한 Ba의 조성을 보였으며, 천이온도 100K 인 Bi계에서는 약한 반자성효과 때문에 추출이 불가능하였다.