The effects of an addition of ZrO2 on the microstructure and electrical properties of MgO films as a protective layer for AC plasma display panels were investigated. MgO + a 200 ppm ZrO2 protective layer prepared by e-beam evaporation exhibited a secondary electron emission coefficient (γ) that was improved by 21% compared to that of a pure MgO protective layer. The relative density and Vickers hardness increased with a further addition of ZrO2. These results suggest that the discharge properties and optical properties of MgO protective layers are closely related to the relative density and Vickers hardness. The good optical and electrical properties of γ, at 0.080, a grain size of 19 μm and an optical transmittance of 91.93 % were obtained for the MgO + 200 ppm ZrO2 protective layer sintered at 1700˚C for 5 hrs.

교류구동형 플라즈마 표시소자의 보호막으로 사용되는 MgO의 특성향상을 위하여 기존의 MgO에 양이온이 등전적으로 치환될 수 있는 ZnO를 소량 첨가하여 고주파 마그네트론 스퍼터링 방법으로 Mg1-xZ nxO박막을 성장시키고 박막의 전기적, 광학적 특성을 조사하였다. ZnO농도가 0.5 at%, 1at%인 Mg1-xZ nxO 박막을 보호막으로 갖는 PDP 테스트 판넬을 제작하고 ZnO의 첨가가 소자의 방전전압과 메모리 이득에 미치는 영향을 살펴보았다. ZnO농도가 0at%, 0.5 at%, 1at%인 Mg1-xZ nxO 박막의 광투과율은 ZnO 첨가에 따라 변화를 보이지 않으나 유전상수는 다소 증가하는 경향을 보였다. ZnO의 농도가 0.5 at%인 Mg1-xZ nxO 박막을 보호막으로 갖는 PDP 소자의 방전개시전압과 방전유지 전압이 MgO 박막을 보호막으로 갖는 소자에 비해 20V까지 낮아졌고, 결과적으로 메모리계수는 다소 증가하였다. ZnO농도가 0.5 at%, 1at%인 Mg1-xZ nxO 박막을 보호막으로 갖는 소자에서 ZHO의 첨가에 비례하여 방전세기 (플라즈마 밀도)가 증가하였다.도)가 증가하였다.도)가 증가하였다.