Candelilla wax-in-water nanoemulsions stabilized by Span 80/Tween 80 were prepared by the phase inversion composition (PIC) method. Stable nanoemulsions with droplet diameters below 50 nm could be formed when the hydrophilic–lipophilic balance (HLB) values were between 13.5 and 14.5, surfactant concentration was 5.0 wt%, and the surfactant-wax ratio was 1:1. Increased emulsification temperature and cooling rate were found to improve the emulsion properties. Process of PIC (adding aqueous phase to the wax phase) produced smaller droplet size nanoemulsion compared to the process of adding wax phase to the aqueous phase. The stability of these nanoemulsions was assessed by following the change in droplet diameters with time of storage at room temperature (∼25 °C). The size remained constant during 2 months storage time.

본 연구에서는 정제수/Span 80-Nikkol BL 25/오일계의 water-in-oil (W/O) 나노에멀젼을 높은 온 도에서 PIC 유화로 제조하였다. 이 방법은 본 시스템에서 미세하게 분산된 저점도의 W/O 나노에멀젼의 형성을 가능케 하였다. 그러나 실온에서 PIC 방법으로 제조된 에멀젼은 나노에멀젼보다는 마크로에멀젼이 제조되었다. 유화온도가 30 ℃에서 80 ℃로 증가하면 온도에 따른 계면장력의 큰 변화의 결과로 입자 크기는 2 μ m에서 100 nm 정도로 감소하였다. 80 ℃에서 제조된 나노에멀젼의 입자 크기는 50 ∼ 200 nm 범위에 있었고 내상의 분율 은 15 wt%까지 가능하였다. 또한 혼합 유화제의 최적 HLB는 7.0 부근에서 가장 안정한 나노에멀젼이 형성되었 다. 제조된 나노에멀젼은 1개월 이상 실온에서 안정하였다. 본 연구 결과는 저점도의 W/O 나노에멀젼의 형성 최적화에 중요한 정보를 제공할 수 있다. 이 결과는 W/O 나노에멀젼의 저점도로 인한 부드러운 사용감 등으로 화장품 제형으로 유용하게 이용될 것으로 생각된다.