Effects of the amount of nickel powder (Ni) in Ni-carbon fiber (CF) hybrid filler systems on the conductivity(or resistivity) and thermal coefficient of resistance (TCR) of filled high density polyethylene were studied. Increases of the resistivity and TCR with increasing Ni concentration at a given hybrid filler content were observed. Using the fiber contact model, we showed that the main role of Ni in the hybrid filler system is to decrease the interfiber contact resistance when Ni concentration is less than the threshold point. The formation of structural defects leading to reduced reinforcing effect resulted in both a reduction of strength and an increase of the coefficient of thermal expansion in the composite film; these changes are responsible for the increases of both resistivity and TCR with increasing Ni concentration in the hybrid filler system.

연구는 음식물 쓰레기를 음식물 소멸기에서 미생물에 의해 발효하여 유기물을 감량화하고, 음식물 발효시 발생되는 가스를 냉각기에서 기체와 수분으로 분리하여 기체는 반응기로 다시 보내고 수분은 응축하여 침지식 MF 중공사 분리막이 장착된 MBR 시스템에 적용하여 처리하는 시스템에 관한 연구이다. (주)바이오하이테크에서 제작한 음식물 소멸기와 수처리 장치에 침지식 MF 중공사 모듈을 설치하여 90일간 H연구소 직원식당에서 발생되는 음식물 쓰레기를 연속 투입하여 처리하였다. 음식물 소멸기 초기 Seeding를 위하여 수분조절제로 미강, 왕겨, 톱밥을 305 kg 투입하였고 음식물은 운전기간동안 1,648 kg투입하였고 응축폐수는 1,600 L 발생되었다. 음식물 소멸기 운전 종료 후 배출된 발효 부산물은 386 kg으로 감량율은 약 80%로 조사되었다. 침지식 MF 중공사 분리막 모듈을 응축폐수의 MBR 시스템에 적용하여 유기물 처리한 결과 제거율은 각각 BOD 99.9%, COD 97.5%, SS 98.6%, T-N 54.6%, T-P 34.7%였으며, 총대장균은 100%가 제거되었다.

Many of researches regarding mechanical properties of composite materials are associated with humid environment and temperature. Especially the temperature is a very important factor influencing the design of thermoplastic composites. However, the effect of temperature on impact behavior of reinforced composites have not yet been fully explored. An approach which predicts critical fracture toughness GIC was performed by the impact test in this work. The main goal of this work is to study the effect of temperature and span of specimen supports on the results of Charpy impact test for GF/PE composite. The critical fracture energy and failure mechanism of GF/PE composites were investigated in the temperature range of 60℃;to;-50℃ by the Charpy impact test. The critical fracture energy showed the maximum at the ambient temperature, and it tended to decrease as the temperature increased or decreased from the ambient temperature. The major failure mechanisms are the fiber matrix debonding, the fiber pull-out and/or delamination and the matrix deformation.n.

Thermosetting matrix composites have disadvantages in terms of moulding time, repairability and manufacturing cost. Thus the high-performance thermoplastic composites to eliminate such disadvantages have been developed so far. As a result of environmental and economical concerns, there is a growing interest in the use of thermoplastic composites. However, since their mechanical properties are very sensitive to the environment such as moisture, temperature etc., those behaviors need to be studied. Particularly the temperature is a very important factor influencing the mechanical behavior of thermoplastic composites. The effect of temperature have not yet been fully quantified. Since engineering applications of reinforced composites necessitate their fracture mechanic characterization, work is in progress to investigate the fracture and related failure behavior. An approach which predicts the tensile strength was perpormed in the tensile test. The main goal of this work is to study the effect of temperature on the result of tensile test with respect to GF/PE composite. The tensile strength and failure mechanisms of GF/PE composites were investigated in the temperature range 60℃ to -50℃. The tensile strength increased as the fiber volume fraction ratio increased. The tensile strength showed the maximum at -50℃, and it tended to decrease as the temperature increased from -50℃. The major failure mechanism was classified into the fiber matrix debonding, the fiber pull-out, the delamination and the matrix deformation.

변형경화형 시멘트 복합체(SHCC)는 직접인장 상황에서 FRCCs에 비해 우수한 변형경화 특성을 갖는 재료이다. 하지만 SHCC는 일반적인 콘크리트에 비해서 시멘트비율이 높은 부배합 이며, 이에 따라서 자기수축이 큰 특성을 갖는 재료이다. 따라서 시멘트 복합체 내에 팽창재를 대체함으로써 수축저감을 통한 성능향상을 기대하였다. 이 연구에서는 각 강도별 SHCC의 배합에 팽창재를 대체함에 따른 역학적특성을 평가하고자 하였다. 시험결과 설계기준 압축강도 70MPa 배합이 압축, 인장, 휨, 시험에서 우수한 역학적 특성을 나타내었으며, 균열 특성에서는 팽창재를 대체한 SHCC가 균열분산 및 연성에서 우수한 특성을 나타내었다.