To investigate the cyclic characteristics of the retrofitted exterior joints of RC frame with haunch, 70% scaled 6 beam-column exterior joint subassemblies were designed according to design guideline according to 1988 and tested with cyclic loading up to 3.5% story drift ratio. During the experiments axial forces are applied to columns to simulate gravity load. Experimental results shows that the strength of retrofitted specimens was increased steadily until 2.5% story drift ratio and their strengths increased more than 1.7 times of the non-retrofitted in case that main bar was bent away from exterior joint. The joint strength and effective stiffness of the retrofitted specimen was increased and results in more deformation capacity compared to the non-retrofitted.
국내 비내진 설계된 RC 골조 외부접합부의 횡저항 능력특성을 연구하기 위하여, 1988년 이후의 건물을 대상으로 실물 크기의 70%의 T형 보-기둥 실험체 4개를 제작하여 보에 횡력을 가력하여 실험을 수행하였다. 작용한 횡력은 총 9단계로 변위를 조절하여 최대 횡변위비 3.5%까지 가력하였고, 각 변위 단계마다 3싸이클의 반복하중을 가력하였다. 실제의 상황과 유사하게 하기 위하여 실험동안 기둥에 압축력을 지속적으로 작용하였다. 실험 결과, 부재가 휨 공칭강도에 도달하여야 하는 내력에 비하여 실험 결과는 85%이하로 나타났고 층간변위비 0.85% 미만에서 모든 실험체의 접합부에서 전단균열이 발생하여 국내 외부접합부가 취약함을 확인할 수 있었다. 또한 접합부 균열발생시 주응력-층간변위비는 Priestly의 제안식과 유사하게 나타났다.
본 연구에서는 기존 철근콘크리트 건물의 보-기둥 접합부의 내진성능의 개선을 위해 보-기둥 접합부 영역을 FRP보강재(매입형 CFRP Rod, CFRP시트)를 사용하여 보강한 후 내진성능을 평가하였다. 총 6개의 실험체를 제작하고 실험을 수행하여 내진성능을 평가하였으며, 본 연구의 실험결과를 근거로 다음과 같은 결론을 얻었다. 기존 철근콘크리트 보-기둥 접합부의 접합부 영역을 보강한 결과, 초기 재하시 접합부 영역의 균열억제 효과와 재하 전 과정을 통하여 보강재의 구속효과로 인하여 균열억제 효과가 커서 안정적인 파괴형태 및 내력향상 효과를 나타내었다. 매입형 CFRP Rod와 CFRP시트를 활용한 RC 외부 보-기둥 접합부 실험체 RBCJ-SRC2는 표준실험체 RBCJ와 비교하여 변위연성4, 7에서 각각 최대 내력은 1.97배, 에너지소산능력은 2.08배 증가하였다. 또한, 실험체 RBCJ-SR시리즈와 비교하여 최대내력이 1.09~1.11배 증가하였다. 그리고 실험체 RBCJ-CS, RBCJ-SR시리즈, RBCJ-SRC2는 변위연성 5, 6에서 표준실험체 RBCJ 보다 에너지소산능력이 1.10~2.30배 증가하였다. 그리고 에너지소산능력은 변위연성 4에서 13.0~14.4% 증가하였다.
In this study, experimental research was carried out to study the high strength RC exterior beam-column joints regions using reinforcing detailings and high ductile fiber-reinforced mortar.
Test results showed that specimen BCJISP were increased th maximum load-carrying capacity and showed stable hysteresis behavior and satisfactory crack pattern in comparison with th standard specimen BCJC.
In this study, experimental research was carried out to study the high strength RC exterior beam-column joints regions, without the shear reinforcement, using high ductile fiber-reinforced mortar. Test results showed that specimen BCJNSP1.0 were increased th maximum load-carrying capacity and showed stable hysteresis behavior and satisfactory crack pattern in comparison with th specimen BCJNS without shear reinforcement in the beam-column joint region.
In this study, experimental research was carried out to study the high strength RC exterior beam-column joints regions, without the shear reinforcement, using high ductile fiber-reinforced mortar. Specimens designed by retrofitting the exterior beam-column joint regions of existing reinforced concrete building showed a stable mode of failure and an increase in shear strength capacity due to the effect of enhancing dispersion of crack control at the time of initial loading and bridging of fiber from retrofitting new high ductile materials during testing.