The long-period stacking order (LPSO) structures and stacking faults (SFs) in rapidly solidified powder metallurgy (RS P/M) Mg97Zn1Y2 alloy were investigated by high resolution transmission electron microscopy (HRTEM) observations. The 18R-type LPSO structure with a stacking sequence of ACBCBCBACACACBABAB and a period of 4.86 nm was observed in the as-extruded RS P/M Mg97Zn1Y2 alloy. After annealing at 773 K for 5 hr, the 18R-type LPSO structure was transformed to the 14H-type LPSO structure with a stacking sequence of ABABABACBCBCBC and a period of 3.64 nm. The 24R-type LPSO structure containing 24 atomic layers of ABABABABCACACACABCBCBCBC with period of 6.18 nm coexists with the 14H-type LPSO structure in the same grains. The LPSO structures contain intrinsic Type II SFs such as BCB/CABA and ABA/CBCB stacking sequences of a closely packed plane.

In this study the changes of the hardness and microstructures during aging at 120 of an RS-P/M Al-5.6wt%Zn-2.0wt%Mg-1.3wt%Zr-1.0wt%Mn-0.25wt%Cu alloy were studied using a transmission electron microscopy. The hardness increased rapidly at early stage of aging and reached the maximun when the specimen was aged for 24 hr. The many irregular-shaped and rod-shaped dispersoids with 0.1-0.4 m in length were observed in the as-extruded alloy. The dark particles with 2-3 nm in size were observed in aged specimen for 5hr and those are thought to be G.P.zones or precursor of precipitates. In aged specimen for 24 hr, the phases were distributed homogeneously within the matrix and the PFZ with 30-40 nm in width was observed along the grain boundary. With further aging, the width of PFZ increased and phases were also detected within the matrix.