A spin coating process for RRAM, which is a TiN/TiO2/FTO structure based on a PTC sol solution, was developed in this laboratory, a method which enables low-temperature and eco-friendly manufacturing. The RRAM corresponds to an OxRAM that operates through the formation and extinction of conductive filaments. Heat treatment was selected as a method of controlling oxygen vacancy (VO), a major factor of the conductive filament. It was carried out at 100 oC under moisture removal conditions and at 300 oC and 500 oC for excellent phase stability. XRD analysis confirmed the anatase phase in the thin film increased as the heat treatment increased, and the Ti3+ and OH- groups were observed to decrease in the XPS analysis. In the I-V analysis, the device at 100 oC showed a low primary SET voltage of 5.1 V and a high ON/OFF ratio of 104. The double-logarithmic plot of the I-V curve confirmed the device at 100 oC required a low operating voltage. As a result, the 100 oC heat treatment conditions were suitable for the low voltage driving and high ON/OFF ratio of TiN/TiO2/FTO RRAM devices and these results suggest that the operating voltage and ON/OFF ratio required for OxRAM devices used in various fields under specific heat treatment conditions can be compromised.

In this study, solid solution heat treatment of consolidated nickel-based superalloy powders is carried out by hot isotactic pressing. The effects of the cooling rate of salt quenching, and air cooling on the microstructures and the mechanical properties of the specimens are analyzed . The specimen that is air cooled shows the formation of serrated grain boundaries due to their obstruction by the carbide particles. Moreover, the specimen that is salt quenched shows higher strength than the one that is air cooled due to the presence of fine and close-packed tertiary gamma prime phase. The tensile elongation at high temperatures improves due to the presence of grain boundary serrations in the specimen that is air cooled. On the contrary, the specimen that is salt quenched and consists of unserrated grain boundaries shows better creep properties than the air cooled specimen with the serrated grain boundaries, due to the negative creep phenomenon.

Microstructural and mechanical characteristics of Al-6Si-2Cu alloy for lightweight automotive parts were investigated. The test specimens were prepared by gravity casting process. Solution heat treatments were applied to as-cast alloys to improve mechanical properties. The microstructure of the gravity casting specimen presents a typical dendrite structure, having a secondary dendrite arm spacing (SDAS) of 37μm. In addition to the Al matrix, a large amount of coarsened eutectic Si, Al2Cu intermetallic phase, and Fe-rich phases were identified. After solution heat treatment, single-step solution heat treatments were found to considerably improve the spheroidization of the eutectic Si phase. Two-step solution treatments gave rise to a much improved spheroidization. The mechanical properties of the two-step solution heat treated alloy have been shown to lead to higher values of properties such as tensile strength and microhardness. Consequentially, the microstructural and mechanical characteristics of Al alloy have been successfully characterized and are available for use with other basic data for the development of lightweight automotive parts.

환경친화적인 농산물 살균소독 세척방법으로 소성칼슘 및 열처리에 의한 신선편이 브로콜리 저장 중 품질 및 미생물적인 안전성 향상 효과를 구명하기 위하여 본 연구를 수행하였다. 브로콜리를 절단한 뒤 수돗물, 50μL·L-1 염소수 및 1.5g·L-1 소성칼슘 용액과 45℃의 수돗물 열처리, 열처리와 살균소독제를 혼합한 45℃의 1.5g·L-1 소성칼슘 용액에서 각각 2분 세척하였다. 그리고 신선편이 브로콜리를 50μm PE 필름에 포장하여 5℃에서 9일 저장하면서 기체조성, 전기전도도, 미생물수, 색 및 관능적인 품질을 조사하였다. 포장내부의 기체조성은 열처리에서 O2 농도가 낮고, CO2 농도는 높았으나 비열처리구에서는 살균소독 방법 간에 차이가 없었다. 소성칼슘 및 염소수 살균소독처리는 수돗물 처리보다 신선편이 브로콜리의 미생물 감소에 효과적이었고 열처리는 저장 3일까지는 효과가 있었으나 6일 이후에는 나타나지 않았다. 전기전도도는 소성칼슘 + 열처리에서 높게 나타났고, 색은 저장기간이 지나면서 명도가 낮아지고 황색도는 증가하였으나 살균소독 처리간에는 차이가 나타나지 않았다. 신선편이 브로콜리 저장 중 미생물수는 소성칼슘 단독처리가 염소수와 비슷한 수준으로 저장 9일 동안 일반세균수 제어효과를 나타냈고, 대장균군도 수돗물 처리보다 저장기간 내내 적게 나타났다. 또한 브로콜리 절단면의 변색 억제에는 열처리가 효과적이었으나 이취는 높게 나타났으며, 비열처리구에서 소성칼슘 용액처리는 염소수와 같이 수돗물보다 외관이 우수하고, 이취가 적게 나타났다. 따라서 소성칼슘 처리는 환경친화적인 방법으로서 신선편이 브로콜리의 염소 살균소독 세척을 대체할 수 있는 방법으로 판단되었다.