Green BaSi2O2N2:0.02Eu2+ phosphor is synthesized through a two-step solid state reaction method. The first firing is for crystallization, and the second firing is for reduction of Eu3+ into Eu2+ and growth of crystal grains. By thermal analysis, the three-time endothermic reaction is confirmed: pyrolysis reaction of BaCO3 at 900 oC and phase transitions at 1,300 oC and 1,400 oC. By structural analysis, it is confirmed that single phase [BaSi2O2N2] is obtained with Cmcm space group of orthorhombic structure. After the first firing the morphology is rod-like type and, after the second firing, the morphology becomes round. Our phosphor shows a green emission with a peak position of 495 nm and a peak width of 32 nm due to the 4f65d1→4f7 transition of Eu2+ ion. An LED package (chip size 5.6 x 3.0 mm) is fabricated with a mixture of our green BaSi2O2N2, and yellow Y3Al5O12 and red Sr2Si5N8 phosphors. The color rendering index (90) is higher than that of the mixture without our green phosphor (82), which indicates that this is an excellent green candidate for white LEDs with a deluxe color rendering index.

본 연구에서는 생체모방기술을 응용하여 감성의류용 구조발색사를 방사하고, 이를 사용하여 직물을 제직 감량 가공하여 이들의 발색성 및 촉감 물성을 측정하여 감성의류용 용도의 적용성을 확인하여 다음과 같은 연구결과를 얻었다. 삼각단면을 가진 37층의 폴리에스테르와 나일론을 교호로 적층한 구조발색사의 방사조건을 확립하였으며, 이 세 가지 사의 발색성을 multi angle spectro-photometer로 확인하였다. 그리고 이 사들로 제직한 구조발색 직물 세 가지의 겉보기 색차와 반사율을 분석한 결과, 700nm에서 400nm까지의 파장에서 발색성을 확인하였다. 또한, 직물의 밀도와 조직이 다른 세 가지 구조발색 직물을 제직하고 감량 가공 처리하여 직물 역학특성치에서 촉감을 측정한 결과, 100℃, 60분 감량 처리한 시료가 최적설계(194ends/in × 105picks/in) 및 감량 조건임을 확인할 수 있었다. 그리고 감량 처리 시 온도와 처리시간 증가에 따라 감량률이 13%에서 최대 23%까지 증가함을 확인할 수 있었다. 이때 직물의 신축특성, 굽힘강성 및 전단강성은 감소하며 압축특성은 증가하는 현상을 보였다. 그리고 최적설계조건인 1번 직물시료를 100℃, 60분 감량 처리할 때 촉감이 가장 우수하며 일본 몰포 직물보다 더 우수한 촉감치를 얻었다.