The XYZ 3-dimensional thermal conductivities of the C/C up to 2000 °C were measured by a laser flash method. Carbon fiberreinforced carbon composites (C/C) were generally developed for aerospace missions due to their excellent thermal resistivity at ultrahigh temperature. C/C must endure harsh environments such as thousands of degrees Celsius without degradation of its mechanical properties. To solve this problem, among the passive thermal protection system, we suggest a method of conducting more heat through the mono-axial direction, which resulted in ease of the thermal rise in the heat receiving part. For example, the X-43A flight applied unbalanced C/C (UCC) with different carbon fiber orientation ratios according to the XY direction in the leading edge part. To investigate the difference in thermal conductivity between unbalanced C/C (UCC) and balanced C/C (BCC), unbalanced and balanced preforms were prepared by a needle punching process, and then they were densified by pitch infiltration and a carbonization process. We compared and analyzed the effects of unbalanced C/C(UCC) and balanced C/C (BCC) structures on the thermal conductivity. We also designed the “rule of mixtures” equation for calculating thermal conductivities of each C/C using reported data of carbon fiber and graphite matrix. Our calculations of thermal conductivity ratio match the ratio of real data.

With increase in operating temperature of gas turbine for higher efficiency, it is necessary to find new materials of TBC for replacement of YSZ. Among candidate materials for future TBCs, zirconate-based oxides with pyrochlore and fluorite are prevailing ones. In this study, phase structure and thermal conductivities of oxide system are investigated. system are comprised by selecting as A-site ions and as B-site ion in pyrochlore structures. With powder mixture from each oxide, oxides are fabricated via solid-state reaction at . Either pyrochlore or fluorite or mixture of both appears after heat treatment. For the developed phases along compositions, thermal conductivities are examined, with which the potential of compositions for TBC application is also discussed.

This paper reports the microstructures and thermal conductivities of -SiC composite ceramics with size and amount of SiC. We fabricated sintered bodies of -x vol.% SiC (x=10, 20, 30) with submicron and nanosized SiC densified by spark plasma sintering. Microstructure retained the initial powder size of especially SiC, except the agglomeration of nanosized SiC. For sintered bodies, thermal conductivities were examined. The observed thermal conductivity values are 40~60 W/mK, which is slightly lower than the reported values. The relation between microstructural parameter and thermal conductivity was also discussed.