Thermoelectric materials have been the focus of extensive research interest in recent years due to their potential in clean power generation from waste heat. Their conversion efficiency is primarily reflected by the dimensionless figure of merit, with higher values indicating better performance. There is a pressing need to discover materials that increase output power and improve performance, from the material level to device fabrication. This review provides a comprehensive analysis of recent advancements, such as Bi2Te3-based nanostructures that reduce thermal conductivity while maintaining electrical conductivity, GeTe-based high entropy alloys that utilize multiple elements for improved thermoelectric properties, porous metal-organic frameworks offering tunable structures, and organic/hybrid films that present low-cost, flexible solutions. Innovations in thermoelectric generator designs, such as asymmetrical geometries, segmented modules, and flexible devices, have further contributed to increased efficiency and output power. Together, these developments are paving the way for more effective thermoelectric technologies in sustainable energy generation.

A thin film thermoelectric generator that consisted of 5 p/n pairs was fabricated with 1 μm-thick n-type In3Sb1Te2 and p-type Ge2Sb2Te5 deposited via radio frequency magnetron sputtering. First, 1 μm-thick GST and IST thin films were deposited at 250 oC and room temperature, respectively, via radio-frequency sputtering; these films were annealed from 250 to 450 oC via rapid thermal annealing. The optimal power factor was found at an annealing temperature of 400 oC for 10 min. To demonstrate thermoelectric generation, we measured the output voltage and estimated the maximum power of the n-IST/ p-GST generator by imposing a temperature difference between the hot and cold junctions. The maximum output voltage and the estimated maximum power of the 1 μm-thick n-IST/p-GST TE generators are approximately 17.1 mV and 5.1 nW at ΔT = 12K, respectively.