In this work, the trend in the performance of carbon fiber (CF) and its composite during self-polymerization of polydopamine (PDA) at carbon fiber surface was investigated by varying the self-polymerization time of dopamine in an aqueous solution. Research has shown that the PDA coating elevated the surface roughness and polarity of the inert fiber. The tensile strength of single carbon fiber was significantly improved, especially after 9 h of polydopamine self-polymerization, increasing by 18.64% compared with that of desized carbon fiber. Moreover, the interlaminar shear strength (ILSS) of CF-PDA9-based composites was 35.06% higher than that of desized CF-based composites. This research will provide a deep insight into the thickness and activated ingredients of dopamine oxidation and self-polymerization on interfacial compatibility of carbon fiber/epoxy resin composites.

목적: 굴절이상별 세 그룹으로 분류한 우리나라 아동들의 안축장과 빛간섭단층촬영(OCT)로 측정한 황반두께, 망막신경섬유층두께 사이의 상관성을 알아보고자 하였다. 방법: 안질환이 없고 안과관련 수술 경험이 없는 아동 67명(134안)을 대상으로 원시, 정시, 근시 그룹으로 분류하였다. 황반부와 망막신경섬유층두께는 Cirrus HD-OCT를 이용하여 측정하였고, 안축장은 IOL Master를 이용하여 측정하였다. 결과: 안축장은 근시, 정시, 원시그룹 순서로 길게 측정되었다(p<0.05). 중심부황반의 두께는 근시, 정시, 원시그룹 순서로 두껍게 측정되었다(p<0.05). 주변부황반부는위쪽, 코쪽, 아래쪽부분에서 근시그룹이 가장 얇았다(p<0.05).황반의 중심부 두께는 안축장과 양의 상관관계가 있었다(r=0.283, p<0.05). 주변부 황반의 두께는 모두 안축장과 음의 상관관계를 보였다. 귀쪽망막신경섬유층두께(Temporal RNFL Thickness)는 근시그룹이 가장 두꺼운 결과를 보였고,안축장과통계적으로 유의한 양의상관성이 나타났다(r=0.39, p<0.05). 위쪽과 코쪽, 아래쪽의 망막신경섬유층 두께는 안축장과 모두 음의 상관성을 나타냈다. 코쪽 부분의 두께는 통계적으로 유의하게 나타났다(r=-0.23, p<0.05). 결론: 본 연구를 통해 우리나라 소아들의 OCT로 측정한 망막의 황반부의 두께, 망막신경섬유층의 두께와 안축장은 근시의 정도가 높을수록 안축장의 길이가 더 길게 측정되었으며, 굴절이상별 세 그룹에서 나타나는 차이점을 확인하였다.