A metal mesh TCE film is fabricated using a series of processes such as UV imprinting of a transparent trench pattern (with a width of 2-5 μm) onto a PET film, filling it with silver paste, wiping of the surface, and heatcuring the silver paste. In this work nanosized (40-50 nm) silver particles are synthesized and mixed with submicron (250-300 nm)-sized silver particles to prepare silver paste for the fabrication of metal mesh-type TCE films. The filling of these silver pastes into the patterned trench layer is examined using a specially designed filling machine and the rheological testing of the silver pastes. The wiping of the trench layer surface to remove any residual silver paste or particles is tested with various mixture solvents, and ethyl cellosolve acetate (ECA):DI water = 90:10 wt% is found to give the best result. The silver paste with 40-50 nm Ag:250-300 nm Ag in a 10:90 wt% mixture gives the highest electrical conductance. The metal mesh TCE film obtained with this silver paste in an optimized process exhibits a light transmittance of 90.4% and haze at 1.2%, which is suitable for TSP application.

본 연구에서는 flake type hybrid silver powder와 poxy type hybrid binder로 그라비어 오프셋 인쇄용 실버 페이스트를 제조하였다. 제조된 실버 페이스트로 그라비어 오프셋인쇄법을 이용하여 30/30㎛(line/space) 를 연속적으로 300장 인쇄가 가능했다. 130℃에서 20분 동안 오븐에서 경화시켰을 때, 선저항은 약 10.4Ω㎝, 연필경도는 4H였다. 결론적으로 본 연구의 결과는 터치 패널용 narrow bezel전극으로 사용 가능함을 알 수 있었다.

최근 전자 디스플레이에서 각광받고 있는 터치스크린은 급속한 정보화 사회 속에서 비약적인 발전을 거듭하고 있다. 터치패널은 키보드나 마우스와 같은 입력장치를 사용하지 않고, 화면에 나타난 문자나 특정 위치에 사람의 손 또는 물체가 닿으면 그 위치를 파악하여 특정한 기능을 처리하도록 한 패널이다. 이러한 터치스크린에서의 터치패널용 Ag 페이스트는 대부분 열 경화형 페이스트를 사용하고 있다. 이러한 열 경화형 페이스트는 건조공정에 따른 열에너지 소비와 유기용제에 따른 작업환경 개선의 문제점을 가지고 있다. 본 연구에서는 기존에 사용되는 열 경화형 Ag 페이스트가 아닌 친환경적이고 경제적인 UV 경화형 페이스트를 제조하였다. 현재 시판중인 열 경화형 바인더 대신 UV 경화형 올리고머를 사용하였고 유동특성을 부여하기 위해 단관능 모노머를 첨가하여 전도성 Ag paste 패턴형성을 할 수 있었다. 그 결과 열 경화형 Ag 페이스트만큼 접착력, 경도, 내성 등이 우수하였으며 미세패턴의 재현이 가능했으며 스크린 인쇄를 이용한 친환경적인 패터닝 기술로서의 가능성을 확인할 수 있었다.