In recent days, the study of a new phosphorescent phosphor has been performed in order to overcome the defect of sulfide phosphor and increase the brightness and long after-glow characteristic of phosphorescent phosphor. Particularly, sulfide phosphor usually used is so chemically unstable that the study of oxide phosphors are processing. Eu2+, Nd3+ doped Ba-Al-O phosphors sintered at 600~1500℃ for 2hours had the PL emission spectrum and after-glow over 1200℃. In this system, as the mole concentration of alumina increases, emission bands of phosphors moved from 500nm to 380nm. The optimum concentration of flux was 5wt% and after-glow characteristics of phosphors were found at the host material molar ratio (BaCO3:Al2O3), 1:1 and 1:3.

SrAI2O4:Eu2+를 합성하여 장잔광 축광재료로서 가장 중요한 발광특성과 장잔광특성을 조사하였다. 융제로서 B2O3를 3wt% 첨가한 SrCO3, Eu2O3, AI2O34의 혼합분말은 1000˚C이상에서 모체결정인 SrAl2O4의 단일상이 형성되었으나, 장잔관 형광체로서 최적의 합성조건은 1300˚C, 3시간이었다. 그리고 SrAI2O4:Eu2+는 부활제인 Eu2+의 4f65d1 →4f7천이에 기인하여 황록색발광영역의 520nm(2.384eV)를 최대 발파장으로 하는 450~650nm의 폭넓은 발광스펙트럼을 보였으며, 또한 발광파장을 520nm로 고정하여 측정한 여기스펙트럼의 최대 흡수피크는 360nm이고 250nm에서 480nm의 넓은 범위에서 흡수스펙트럼이 관찰되었다.