PURPOSES : The objective of this study is to evaluate the effect of the residual mortar of recycled concrete aggregate on the expansion behavior during alkali silica reaction (ASR). METHODS: In order to evaluate the net effect of residual mortar on ASR expansion behavior, two aggregate samples with the same original virgin aggregate source but different residual mortar volumes were used. ASTM C1260 test was used to evaluate the ASR expansion behavior of these two aggregates and the original virgin aggregate. RESULTS: The greater the amount of residual mortar in recycled concrete aggregates, the less is the induced ASR expansion. Depending on the amount of residual mortar in recycled concrete aggregate, the ASR expansion of recycled concrete aggregate may be less than half of that of the original virgin aggregate. CONCLUSIONS: The residual mortar of recycled concrete aggregate may lead to the under estimation of the ASR expansion behavior of the original virgin aggregate.

국내에서는 콘크리트 포장용 굵은 골재를 대상으로 화학적인 시험방법과 모르타르 봉 시험방법을 이용한 결과 알칼리-실리카 반응 유해 가능성이 낮은 것으로 알려져 왔으나, 최근에 알칼리 - 실리카 반응에 의한 파손이 발생되었고, ASTM C 1260을 이용한 결과 일부 골재에서 유해한 팽창이 발생된다고 보고되었다. 따라서 본 논문에서는 모르타르 봉 시험방법인 KS F 2546과 ASTM C 1260을 이용하여 길이 팽창 유도기간의 환경조건이 알칼리 - 실리카 팽창 반응 특성에 미치는 영향을 평가하고자 하였다. KS F 2546의 경우 대상 골재 모두 반응성 없음으로 판정되었으나 ASTM C 1260에서는 일부 골재에서 잠재반응성 이상으로 판정되었다. 이는 외부로부터의 알칼리 이온의 공급, 온도 및 습도 차이에 의하여 발생한 것으로 판단된다. 또한 ASTM C 1260에서 NaOH의 농도변화 실험을 통하여 NaOH의 농도가 증가할수록 길이팽창이 현저하게 증가한다는 것을 확인하였으며, 온도 및 습도가 증가함에 따라 길이팽창이 증가한다는 것을 확인하였다.

This study suggested an improvement of expansion joint and asphalt pavement construction to prevent pavement and bridges damage due to alkali silica reaction. First, for the case study of alkali silica reaction, we conducted a field survey of expressway 15 Mokpo - Muan. As a result, those following damages were investigated such as abutment tensile cracks, pavement crazing and rising, joint contractions and localized damage etc. To prevent this, we applied those following improvements to Muan2 bridge and Samjeong bridge of expressway 15 and confirmed improvement effectiveness by monitoring. 1) Installing an expansion joint on a bridge near pavement slabs(3 points), 2) constructing asphalt pavement after removing concrete pavement(6m). In conclusion, through such improvements suggested above, we expect that we will be able to effectively prevent bridges damage due to Alkali Silica Reaction. Consequentially, it will also contribute improving the safety of vehicles in the expressway.

The object of this research is to confirm the effect of Waste Glass Sludge on properties of concrete through compressive strength and Alkali-Silica reaction of concrete and to develop as construction material.

Limestone powder can be used for concrete as a partial replacement of Portland cement so that concrete becomes more environment-friendly construction material. One of the great applications of limestone powder added cement concrete might be a cement concrete pavement since the concrete pavement consumes massive quantity of Portland cement. However, it has been reported recently that Alkali-Silica Reaction (ASR) occurs on the cement concrete pavement causing a serious damage. This study investigates the resistance of limestone powder added cement mortar to ASR. The mortar used very high reactive silicious aggregate for accelerated ASR. Experimental procedures followed ASTM C 1260 and variables included different replacement levels of limestone powder in the mortar mix.

To clarify the load-carrying behavior of RC beams caused by the rebar fracture and the expansive crack along the longitudinal reinforcement due to aggregate expansion simulating ASR, experimental study was carried out. From the test result, all specimens caused by the rebar fracture failed in shear tension. Moreover, cracking behavior and crack propagation highly influenced by the range of expansive crack.

알칼리-실리카반응은 시멘트 내의 알칼리와 화학적으로 불안정한 반응성 골재와의 화학반응으로서, 그 결과 콘크리트의 팽창과 균열을 발생하는 작용이다 본 연구에서는 우수한 포조란반응 특성을 나타내는 새로운 광물혼화재로 부각되고 있는 메타카오린의 알칼리-실리카반응 억제 효과에 대하여 연구하였다. 다양한 치환율로 메타카오린을 혼합한 모르타르 공시체를 제작하여, 알칼리-실리카 반응성 시험(ASTM C 1260), 압축강도 시험 및 유동성 시험을 실시하고, 시멘트 수화물에서의 구성성분 변화에 대한 XRD 정량분석을 실시하였다. 그 결과, 메타카오린의 혼합은 시멘트 페이스트내의 가용 포트랜다이트의 함량을 급속히 감소시키는 빠른 포조란반응 및 수화반응 특성을 나타내어, 알칼리-실리카 반응에 의한 팽창을 억제하고 우수한 압축강도를 발현하는 것으로 나타났다. 시멘트에 메타카오린의 혼합에 의한 알칼리-실리카 반응에 의한 팽창억제는 치환율 15% 이상, 즉 시멘트 페이스 내의 가용 포트랜다이트 함량이 약 10% 이하가 될 경우 효과적이다. 메타카오린의 혼합에 의한 알칼리-실리카 반응에 의한 팽창 억제는 유해성이 높은 알칼리-칼슘-실리카 겔의 형성이 억제된 결과와 포조란 효과에 의한 치밀하고 균질한 시멘트 페이스트 형성으로 인한 알칼리 용액의 침투가 억제된 결과에 의한 것으로 생각된다. 15% 이상의 메타카오린의 혼합은 보통의 모르타르보다 높은 초기강도를 발현하였으며, 후기강도는 전 치환율 범위에서 보통의 모르타르 이상의 아주 우수한 강도를 나타내었다. 강도발현 특징은 메타카오린에 의한 빠른 포조란반응 및 수화특성을 반영하고 있다.