PURPOSES : The purpose of this study is to verify the effectiveness of the developed ultra-thin-continuously reinforced concrete partition (UT-CRCP) overlay method through a comparative analysis of the early-behavior of the UT-CRCP with a 100 mm cutting overlay of the existing JPCP. METHODS : This study aims to minimize the vulnerability of the existing JPCP (joint section behavior) by overlaying the continuous reinforcement form to constrain joint behavior. For this purpose, the early-behavior of the JPCP section was measured and the early-behavior of the UT-CRCP section was compared with that of the cutting overlay of the same section. The testbed was constructed for comparative analysis of the two types of pavements and the early behavior was measured using the pure environmental loads, i.e., situations where there was no traffic load. For the UT-CRCP, which is a comparative test group, UT-CRCP was constructed approximately one year after the JPCP was constructed by milling the top of the existing JPCP by 100 mm. RESULTS : 1) UT-CRCP was shown to effectively reduce the amount of crack width change on the surface by 17 %, compared to JPCP, by placing reinforcement inside the pavement. 2) The restricting effect of the UT-CRCP was analyzed by comparing the strain generated by the cross-section depth for the two pavement types. As a result, the restricting rate by depth (20, 80, 120, and 280 mm) was 68.4 %, 80.2 %, 89.2 %, and 26.7 %, respectively. 3) We reviewed the comprehensive gauge restricting rate at depths of 80 mm and 120 mm (80.2 % and 89.2 %, respectively) and the absolute value of behavior that is located at the ±20 mm of the interface of JPCP and UT-CRCP. Thus, it was possible to estimate that both layers of pavements exhibit the same behavior (tied) at the interface between the two pavement layers. CONCLUSIONS : In this study, the early behavior of the BCO concept UT-CRCP overlay technique was analyzed and quantitatively presented to overcome the limitations of JPCP with relatively weak point behavior and to increase the commonality of aged concrete pavement to the performance of the new pavement.

In a wide spectrum of pavement rehabilitation techniques, the application of thin asphalt overlay on existing concrete pavements have shown its ability to restore the functional capacity of the pavement system as well as maintain structural capacity. Although, prior researches stated that it does not add to the structural capacity of the existing pavement, the insulation generated by the asphalt overlay can affect the behavior of the discontinuities in the continuously reinforced concrete pavement (CRCP) system by reducing the magnitude of its movement. The investigation of crack movement behaviors of the CRCP in Chungbu Expressway was conducted in 2-phases: without overlay and with overlay. Crackmeters were installed at selected crack locations and measurements were collected. In the second phase of the investigation, crackmeters were installed at the concrete layer of the CRCP before a 2-inch asphalt overlay was applied. Results have shown that the crack movements under a thin asphalt overlay have reduced by 80% which indicates an effective insulation of the CRCP.

본 연구에서는 노후 콘크리트 포장의 효율적 유지보수를 위하여 국내 최초 적용된 연속철근 콘크리트 개념의 얇은 덧씌우기 공법(CRCO : Thin Bonded Continuously Reinforced Concrete Overlay)의 거동 특성을 살펴보았다. 서해안 고속도로의 폐도 구간에 CRCO 공법과 JCO 공법(Jointed Concrete Overlay)을 시험시공 하였으며, CRCO 공법에 삽입된 종방향 철근으로 효과를 검토하였다. 시험시공 후 균열 조사 결과, CRCO 구간의 기존 줄눈부에서부터 반사 균열이 발생하였으나 그 폭은 매우 좁았다. 철근의 구속역할로 인해 CRCO 공법에서 더 많은 균열이 발생하였으며, 그 간격은 CRCP 보다 더 좁았다. 부착강도 측정 결과, 표면 처리로 Cold Milling 후 이물질을 제거하여 초기에 층간 부착 문제가 발생하지 않았다. 기존 JCP의 줄눈부에 수평으로 매설한 계측기 데이터분석 결과, 초기 균열 터짐 시 일정 폭 이상으로 벌어지지 못하게 종방향 철근이 잡아주는 역할을 하였으며, 온도변화에 대한 수평 변위 발생 억제 효과도 있었다. 하지만 층간 부착 문제가 발생할 경우, 철근의 구속 효과는 저감되었다. 수직 계측기의 데이터를 통해서 철근이 없는 JCO 공법에 비해 CRCO 공법은 종방향 철근 위치에서 층간 부착 문제가 발생하지 않았으며, 현장 코어링 작업을 통해 이를 확인하였다. 슬래브 내의 수평 거동을 분석한 결과, 초기에 철근의 구속으로 인해 CRCO 공법에서는 인장 변형률이, 구속이 미미한 JCO 공법은 압축력이 발생하였다. FWD 데이터 분석 결과, CRCO 공법의 처짐량이 JCO 보다 더 적게 발생하였으며, 지지력 평가에서는 전반적으로 덧씌우기 후가 더 크게 나타났으며, 특히 CRCO 공법이 JCO 공법에 비해 지지력에 대한 덧씌우기 두께 효과가 더 컸다.

본 연구에서는 노후 콘크리트 포장의 효율적 유지보수를 위하여 국내 최초 적용된 Thin Bonded Continuously Reinforced Concrete Overlay (CRCO) 공법의 초기 공용성이 평가되었다. 서해안 고속도로의 표층 파손 구간에 Jointed Plain Concrete Pavement (JPCP) 덧씌우기와 CR8O 공법을 이용한 보수가 진행되었다. JPCP 덧씌우기 공법이 적용된 구간에서는 인접 슬래브가 완전히 분리되도록 덧씌워진 층의 줄눈을 완전히 커팅하였으며, CRCO 공법이 적용된 구간에서는 0.5% 종방향 철근과 위치 고정용 횡방향 철근을 설치한 후 그 위에 덧씌우기를 수행하였다. 두 구간 모두에서 3종시멘트가 이용되었다. 현장 강도 시험 결과, 1~3일 내에 교통개방이 가능한강도가 발현된 것이 확인되었으며, vibrating wire gauge (VWG) 데이터 분석 결과 CRCO 공법이 기존 포장의 줄눈 거동을 억제하는 것으로 나타났다. 부착강도 시험결과, 재령에 상관없이 높은 부착강도가 확인되었다. 한편 JPCP 덧씌우기 공법이 적용된 구간에서는 중앙부에서, CRCO 공법이 적용된 구간에서는 CRCO 포장과 같은 무작위 횡방향 균열이 관찰되었으며, CRCO 공법의 균열폭 거동이 JCP 보다 50% 정도 낮은 것으로 나타났다.