Poly(vinylidene fluoride-trifluoroethylene) (PVDF-TrFE) is a promising ferroelectric polymer for flexible electronics and energy-harvesting devices, owing to its high piezoelectric coefficient and mechanical flexibility. Here, we report that electrohydrodynamic instability induces the formation of closely packed nanostructures on PVDF-TrFE thin film. Intriguingly, the strong electric field used in the fabrication process drives the polymeric fluid of PVDF-TrFE upwards to form the surface structures, facilitating molecular dipole alignment and crystalline ordering. This effect contributes to improved crystal alignment, as confirmed by enhanced X-ray diffraction and Raman characteristic peaks. The nanostructured PVDF-TrFE films exhibit enhanced dielectric properties including permittivity, dielectric loss, and ferroelectric polarization. Notably, P-E loop measurements showed a larger remnant polarization and higher saturation polarization in the nanostructured PVDF-TrFE films, indicating improved ferroelectric behavior. Our results suggest that the electrohydrodynamic instability provides a simple but effective route to simultaneously tailor the surface morphology, crystalline phase, and electrical performance of PVDF-TrFE films.

비열살균기술로서 저온플라즈마 활용 가능성을 탐색하고자 유전체장벽 방전 플라즈마(DBDP)생성장치를 제작하여 최적 플라즈마생성 조건을 도출하고 Staphylococcus aureus를 대상으로 살균성능을 조사하였다. DBDP생성장치는 전력공급장치, 변압기, 전극, 시료처리부 등 네 부분으로 구성하였다. 인가전압은 단상 200 V AC를 사용하고, 변압기를 통하여 10.0-50.0 kV로 변환하고 10.0-50.0 kHz의 주파수의 펄스 구형파를 유전체인 세라믹 블록 내에 장치한 전극에 투입함으로써 상압에서 플라즈마를 생성하였다. 주파수를 올림에 따라 높은 전류가 유입되었고, 이에 비례하여 전력소비량이 증가하였다. 전류세기 1.0-2.0 A, 주파수 32.0-35.3 kHz 범위에서 균일하고 안정적인 플라즈마 발생이 이루어졌으며 시료를 투입하지 않은 상태에서의 최적 전극간격은 1.85 mm 이었다. 전극간격을 높임에 따라 소비 전력이 증가하였으나 시료 처리에 적합한 전극간격은 2.65 mm였다. DBDP 처리에 의한 온도상승은 최대 20oC에 불과하여 열에 의한 생물학적 효과는 무시할 수 있었으며 따라서 비열기술임이 확인되었다. Staphylococcus aureus를 대상으로 DBDP 처리할 경우 초기 5분 동안은 살균치가 직선적인 증가를 보이다가 이후 다소 완만해지는 경향을 보였으며 1.25 A에서 10분간 처리 시 살균치는 5.0을 상회하였다.