Carbon composites for flexible fiber heating element were examined to improve the electrical conductivity in this study. Carbon composites using carbon black, denka black, super-c, super-p with/without CNF or dispersant such as BCS03 and Sikament-nn were prepared. Carbon composite slurry was coated on plane film and yarns(cotton, polyester) and the performances of prepared heating materials were investigated by checking electrical surface resistance, adhesion strength. The plane heating element using carbon black under natural drying condition(25℃) had better physical properties such as surface resistance(185.3 Ohm/sq) and adhesion strength(above 90%) than those of other carbon composite heating elements. From these results, polyester heating element coated by carbon black showed better electrical line resistance(33.2 kOhm/cm) than cotton heating element. Then, it was found that polyester heating element coated by carbon black with CNF(3 wt%) and BCS03(1 wt%) appeared best properties(0.604 kOhm/cm).

본 연구는 피복자재와 전기발열체에 의한 포도 유목의 휴면기와 수액이동기 꽃눈 피해를 경감하기 위하여 수행하였다. 1. 저온 환경제어시스템에서 보온력 차이는 볏짚 +부직포 > 부직포 > 볏짚 > 무피복 순으로 높았으며, 볏짚 +부직포 2중피복에서 온도 저하 지연 효과가 가장 좋았으나, 12시간 처리에서는 피복자재별 보온력 차이가 거의 없었다. 2. 휴면기 꽃눈 피해는 캠벨얼리와 MBA가 비슷하였으며, 거봉에서 높았고, 무피복 > 볏짚 > 부직포 > 볏짚 +부직포 순으로 낮았다. 볏짚 +부직포는 −20℃ 6시간 저온처리부터 꽃눈 피해가 발생하여 보온 효과가 높았다. 3. 수액이동기 –10℃ 저온처리에서 꽃눈 피해는 휴면기와 비슷한 경향이었으며, 품종 간에는 차이가 없었으며, 휴면이타파된 수액이동기 저온에서 꽃눈 피해가 더 크다. 4. 전기발열체 +부직포는 −5℃ 3시간 처리에서 휴면기 –20℃에서 −4.8℃, 수액이동기는 −10℃에서 −4.3℃ 주간부 내부온도가 유지되어 방한에 효과적이었다. 5. 짚 +부직포은 휴면기에는 꽃눈 피해가 발생하는데 지연 효과가 있으나 수액이동기에는 효과가 적었으며, −5℃ 설정 전기발열체 +부직포에서는 꽃눈 피해가 발생하지 않았다.