The purpose of this study is to prepare WO3 nanopowders by high-energy milling in mixture gas (7 % H2+Ar) with various milling times (10, 30, and 60 min). The phase transformation, particle size and light absorption properties of WO3 nanopowders during reduction via high-energy milling are studied. It is found that the particle size of the WO3 decreases from about 30 μm to 20 nm, and the grain size of WO3 decreases rapidly with increasing milling time. Furthermore, the surface of the particles due to the pulverization process is observed to change to an amorphous structure. UV/Vis spectrophotometry shows that WO3 powder with increasing milling times (10, 30, 60 min) effectively extends the light absorption properties to the visible region. WO3 powder changes from yellow to gray and can be seen as a phenomenon in which the progress of the color changes to blue. The characterization of WO3 is performed by high resolution X-ray diffractometry, Field emission scanning electron microscopy, Transmission electron microscopy, UV/Vis spectrophotometry and Particle size analysis.
A Nanosized WO3 and CuO powder mixture is prepared using novel high-energy ball milling in a bead mill to obtain a W-Cu nanocomposite powder, and the effect of milling time on the structural characteristics of WO3-CuO powder mixtures is investigated. The results show that the ball-milled WO3-CuO powder mixture reaches at steady state after 10 h milling, characterized by the uniform and narrow particle size distribution with primary crystalline sizes below 50 nm, a specific surface area of 37 m2/g, and powder mean particle size (D50) of 0.57 μm. The WO3-CuO powder mixtures milled for 10 h are heat-treated at different temperatures in H2 atmosphere to produce W-Cu powder. The XRD results shows that both the WO3 and CuO phases can be reduced to W and Cu phases at temperatures over 700oC. The reduced W-Cu nanocomposite powder exhibits excellent sinterability, and the ultrafine W-Cu composite can be obtained by the Cu liquid phase sintering process.
Mechanical coating process was applied to form 89 %-hydrolyzed poly vinyl alcohol (PVA) onto
boron carbide (B4C) nanopowder using one step high energy ball mill method. The polymer layer coated on the
surface of B4C was changed to glass-like phase. The average particle size of core/shell structured B4C/PVA was
about 50 nm. The core/shell structured B4C/PVA was formed by dry milling. However, the hydrolyzed PVA of
98~99% with high glass transition temperature (Tg) was rarely coated on the powder. The Tg of polymer materials
was one of keys for guest polymer coating on to the host powder by solvent free milling.
활석은 T-O-T 구조의 함수 마그네슘 층상규산염 광물로서, 화학적 안정성과 흡착성 등의 특성을 가지고 있어 다양한 산업분야에서 첨가제, 코팅제 등으로 활용되어 왔다. 최근 나노 복합체의 안정성 향상을 위한 첨가제로서 활석 나노입자가 각광받고 있다. 본 연구에서는 고에너지 볼 밀을 이용하여 기계적인 방법으로 활석 나노입자를 형성하고, 분쇄시간에 따른 입자크기 및 결정도의 변화를 알아보고자 하였다. X-선 회절 분석 결과, 분쇄가 진행됨에 따라 활석의 피크 폭이 점진적으로 증가하여720분 분쇄 후, 활석은 비정질에 가까운 X-선 회절패턴을 보여준다. 레이저회절 입도 분석 결과, 약12 μm이었던 활석의 입도는 분쇄가 진행됨에 따라 약 0.45 μm까지 감소하였으나, 120분 이상 분쇄를진행하여도 뚜렷한 입도의 감소가 관찰되지 않았다. 반면, BET 비표면적은 분쇄 720분까지 꾸준히 증가하여, 분쇄에 따른 입도 또는 형태의 변화가 지속적으로 일어남을 지시한다. 주사전자현미경 및 투과전자현미경 관찰 결과, 720분 분쇄 후 약 100~300 nm 내외의 층상형 입자들이 마이크로 스케일의응집체로 존재함을 확인하였다. 이와 같은 결과는 분쇄시간이 증가함에 따라 활석의 입자크기 및 형태는 지속적으로 변화하지만, 나노입자의 특성상 재응집이 일어나 마이크로 크기의 응집체를 형성하고 있음을 지시한다. 또한 활석의 분쇄에서 판의 크기, 즉 a축, b축 방향의 길이는 감소 한계가 존재하며, 분쇄가 진행될수록 판의 두께, 즉 c축 방향의 길이 감소가 주된 분쇄 메커니즘으로 생각된다. 본연구의 결과는 나노 활석의 형성 메커니즘에 대한 이해를 고양할 수 있을 것으로 기대된다.