        1.
        2014.02 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Bi2Sr2CaCu2Ox(Bi-2212) and Bi2Sr2Ca2Cu3Oy(Bi-2223) high-Tc superconductors(HTS) have been manufactured by plasma spraying, partial melt process(PMP) and annealing treatment(AT). A Bi-2212/2223 HTS coating layer was synthesized through the peritectic reaction between a 0212 oxide coating layer and 2001 oxide coating layer by the PMP-AT process. The 2212 HTS layer consists of whiskers grown in the diffusion direction. The Bi-2223 phase and secondary phase in the Bi-2212 layer were observed. The secondary phase was distributed uniformly over the whole layer. As annealing time goes on, the Bi-2212 phase decreases with mis-orientation and irregular shape, but the Bi-2223 phase increases because a new Bi-2223 phase is formed inside the pre-existing Bi-2212 crystals, and because of the nucleation of a Bi-2223 phase at the edge of Bi-2212 crystals by diffusion of Ca and Cu-O bilayers. In this study the spray coated layer showed superconducting transitions with an onset Tc of about both 115 K, and 50 K. There were two steps. Step 1 at 115 K is due to the diamagnetism of the Bi-2223 phase and step 2 at 50 K is due to the diamagnetism of the Bi-2212 phase.
        4,000원
        2.
        1992.06 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        CeO2를 첨가한 Y-Ba-Cu-0 초전도체를 포정반응을 포함한 준용용법으로 제조하여 미세조직과 초전도성을 관찰하였다. 첨가한 CeO2는 포정반응중에 BaCeO3로 변화하였으며, 이 BaCeO3는 방향성 성장한 1-2-3 초전도상의 기지에 미세하게 분산된다. 초전도체의 TC는 첨가된 CeO2함량에 관계없이 90K 이상으로 매우 높았다. 이는 준용융공정을 적용함으로서 제2상물질을 초전도상으로부터 분리할 수 있었기 때문으로 사료된다.
        4,000원